Significance of Alloying Element Levels in Realizing the Specified Tensile Properties in 18 Wt % Nickel Maraging Steel
ABSTRACT
Among the various grades of commercially available 18 wt. % nickel maraging steels, the one with nominal 0.2% proof strength in the range 1700-1750 MPa is the most commonly used and is distinguished by an excellent combination of high strength and high fracture toughness. The main alloying elements are nickel, cobalt, molybdenum and titanium. The first three of these are present at relatively high concentrations in the chemical composition. The high cost of these metals leads to a high cost of production and this becomes a deterrent to extensive use of the steel. In the present study, an attempt was made to produce the steel by pegging the levels of these alloying elements in the lower half of the specified range. The objective was to save on the raw material cost, while still conforming to the specification. The steel so produced could not, however, attain the specified tensile properties after final heat treatment. The observed behavior is explained based on the role played by the different alloying elements in driving the precipitation hardening reaction.

Cite this paper
nullM. Rao and K. Sivasubramanian, "Significance of Alloying Element Levels in Realizing the Specified Tensile Properties in 18 Wt % Nickel Maraging Steel," Materials Sciences and Applications, Vol. 2 No. 8, 2011, pp. 1116-1120. doi: 10.4236/msa.2011.28150.
References
[1]   R. K. Wilson, “Maraging Steels: Recent Developments and Applications,” The Minerals, Metals & Materials Society, Warrendale, Pennsylvania, 1988.

[2]   M. N. Rao, “Progress in Understanding the Metallurgy of 18% Nickel Maraging Steels,” International Journal of Materials Research, Vol. 97, No. 11, November 2006, pp. 1594-1607.

[3]   “NiMark Alloy 250,” Internet Available: http://www.cartech.com/ssalloysprod.aspx?id

[4]   P. P. Sinha, D. Sivakumar, T. Tharian, K. V. Nagarajan and D. S. Sarma, “Thermal Embrittlement in 18Ni Cobalt Free and 18Ni-8Co-5Mo Maraging Steels,” Materials Science and Technology, Vol. 12, November 1996, pp. 945-954.

[5]   P. P. Sinha, K. Sreekumar, N. S. Babu, B. Pant, A. Natarajan and K. V. Nagarajan, “Development of Heat Treatment Parameters to Improve Fracture Toughness and Grain size of an Embrittled Maraging Steel,” Journal of Heat Treating, Vol. 9, No. 2, 1992, pp. 125-131. doi.org/10.1007/BF02833148

[6]   P. Wuerzinger, R. Rabitsch R and W. Meyer, “Production of Maraging Steel Grades and the Influence of Specified and Nonspecified Elements for Special Applications,” Journal of Materials Science, Vol. 39, No. 24, 2004, pp. 7295-7302. doi.org/10.1023/B:JMSC.0000048744.03279.ec

[7]   W. Sha, A. Cerezo and G. D. W. Smith, “Phase Chemistry and Precipitation Reactions in Maraging Steels: Part IV, Discussion and Conclusions,” Metallurgical Transactions A, Vol. 24A, No. 6, June 1993, pp. 1251-1256. doi.org/10.1007/BF02668193

[8]   A. G. Haynes, “The Making, Shaping and Heat Treating of 18% Ni Maraging Steels,” Proceedings of ASPA Seminar, Madras, 1978, p 38

 
 
Top