Synergistic Reinforcement of Phenol-Formaldehyde Resin Composites by Poly(Hexanedithiol)/Graphene Oxide
Author(s) Jingliang Wei1, Chun Wei1,2,3, Le Su1, Jun Fu1, Jian Lv1,2,3*
ABSTRACT
In this paper, the preparation of graphene oxide was achieved by Hummers method and the surface modification was achieved by poly(hexaneditiol), which was a synthetic thermotropic liquid crystalline polymer. The c-PHDT/GO/PF composites were prepared by blending, rolling and compression molding techniques. Then, the as-prepared samples were characterized by FTIR, Raman, XRD, TGA and POM to obtain information on their structures and properties. After that, the effects of c-PHDT/GO content on the mechanical properties, friction performance and dynamic mechanical performance of c-PHDT/GO/PF composites were studied by Mechanical and Dynamic Mechanical Analysis (DMA) methods. Also, Scanning Electron Microscope (SEM) was used for the characterization of wear and fracture surface morphology. The results revealed that the reinforcing effect of c-PHDT/GO was significant as a considerable enhancement on the mechanical performance of c-PHDT/GO/PF composite as compared to pure phenol-formaldehyde composites was observed: the impact strength, bending modulus and bending strength increased from 1.63 kJ/m2, 8.61 GPa and 41.55 MPa to 2.31 kJ/m2, 10.16 GPa and 54.40 MPa respectively at the c-PHDT/GO content = 0.75%. Moreover, the initial storage modulus increased by 28.4%, while the wear mass loss decreased by 17.8%. More importantly, the reinforcement by c-PHDT/GO was further enhanced as compared to GO/PF and p-PHDT/GO/PF composites, the impact strength of c-PHDT/GO/PF composite increased by 27.6% and 11.1%, the bending strength increased by 11.8% and 7.6%, the initial storage modulus increased by 16.2% and 4.2% and the mass loss due to wear decreased by 12.7% and 8.8%, respectively. Based on these results, we can conclude that the surface modification of GO by poly(hexanedithiol), which includes synergistic effect by c-PHDT and GO, improves the interfacial adhesion between GO and the resin matrix, thus reinforcing the composites.

Cite this paper
Wei, J. , Wei, C. , Su, L. , Fu, J. and Lv, J. (2015) Synergistic Reinforcement of Phenol-Formaldehyde Resin Composites by Poly(Hexanedithiol)/Graphene Oxide. Journal of Materials Science and Chemical Engineering, 3, 56-70. doi: 10.4236/msce.2015.38009.
References
[1]   Novoselov, K.S., Geim, A.K., Morozov, S.V., Jiang, D., Zhang, Y., Dubonos, S.V., et al. (2004) Electric Field Effect in Atomically Thin Carbon Films. Science, 306, 666-669.
http://dx.doi.org/10.1126/science.1102896

[2]   Balandin, A.A., Suchismita, G., Bao, W., Calizo, I., Teweldebrhan, D., Miao, F. and Lau, C.N. (2008) Superior Thermal Conductivity of Single-Layer Graphene. Nano Letters, 8, 902-907.
http://dx.doi.org/10.1021/nl0731872

[3]   Stoller, M.D., Park, S., Zhu, Y., An, J. and Ruoff, R.S. (2008) Graphene-Based Ultracapacitors. Nano Letters, 8, 3498- 3502.
http://dx.doi.org/10.1021/nl802558y

[4]   Lee, C., Li, Q.Y., Kalb, W., Liu, X.Z., Berge, H., Robert, W.C. and Hone, J. (2010) Frictional Characteristics of Atomically Thin Sheets. Science, 328, 76-80.
http://dx.doi.org/10.1126/science.1184167

[5]   Lee, C., Wei, X., Li, Q., Carpick, R., Kysar, J.W. and Hone, J. (2009) Elastic and Frictional Properties of Graphene. Phys. Status Solidi B, 246, 2562-2567.
http://dx.doi.org/10.1002/pssb.200982329

[6]   Lee, C., Wei, X., Kysar, J.W. and Hone, J. (2008) Measurement of the Elastic Properties and Intrinsic Strength of Monolayer Graphene. Science, 321, 385-388.
http://dx.doi.org/10.1126/science.1157996

[7]   Liang, J., Wang, Y., Huang, Y., Ma, Y., Liu, Z., Cai, J., et al. (2009) Electromagnetic Interference Shielding of Graphene/Epoxy Composites. Carbon, 47, 922-925.
http://dx.doi.org/10.1016/j.carbon.2008.12.038

[8]   Ramanathan, T., Abdala, A.A., Stankovich, S., Dikin, D.A., Herrera-Alonso, M., Piner, R.D., et al. (2008) Functionalized Graphene Sheets for Polymer Nanocomposites. Nature Nanotechnology, 3, 327-331.
http://dx.doi.org/10.1038/nnano.2008.96

[9]   Stankovich, S., Piner, R.D., Nguyen, S.B.T. and Ruoff, R.S. (2006) Synthesis and Exfoliation of Isocyanate-Treated Graphene Oxide Nanoplatelets. Carbon, 44, 3342-3347.
http://dx.doi.org/10.1016/j.carbon.2006.06.004

[10]   Verdejo, R., Barroso-Bujans, F., Rodriguez-Perez, M.A., Saja, J.A. and Lopez-Manchado, M.A. (2008) Functionalized Graphene Sheet Filled Silicone Foam Nanocomposites. Journal of Materials Chemistry, 18, 2221-2226.
http://dx.doi.org/10.1039/b718289a

[11]   Ou, J.F., Wang, J.Q., Liu, S., Mu, B., Ren, J.F., Wang, H.G. and Yang, S.R. (2010) Tribology Study of Reduced Graphene Oxide Sheets on Silicon Substrate Synthesized via Covalent Assembly. Langmuir, 26, 15830-15836.
http://dx.doi.org/10.1021/la102862d

[12]   Fang, M., Wang, K., Lu, H., Yang, Y. and Nutt, S. (2009) Covalent Polymer Functionalization of Graphene Nanosheets and Mechanical Properties of Composites. Journal of Materials Chemistry, 19, 7098-7105.
http://dx.doi.org/10.1039/b908220d

[13]   Lu, P., Feng, Y.Y., Zhang, X.Q., Li, Y. and Feng, W. (2010) Recent Progresses in Application of Functionalized Graphene Sheets. Science China Technological Sciences, 53, 2311-2319.
http://dx.doi.org/10.1007/s11431-010-4050-0

[14]   Lei, Y., Wu, Q. and Lian, K. (2006) Cure Kinetics of Aqueous Phenol-Formaldehyde Resins Used for Oriented Strand- board Manufacturing: Analytical Technique. Journal of Applied Polymer Science, 100, 1642-1650.
http://dx.doi.org/10.1002/app.23756

[15]   Jin, Y.Q., Cheng, X.S. and Zheng, Z.B. (2010) Preparation and Characterization of Phenol-Formaldehyde Adhesives Modified with Enzymatic Hydrolysis Lignin. Bioresource Technology, 101, 2046-2048.
http://dx.doi.org/10.1016/j.biortech.2009.09.085

[16]   Lee, W.J., Chang, K.C. and Tseng, I.M. (2012) Properties of Phenol-Formaldehyde Resins Prepared from Phenol-Li- quefied Lignin. Journal of Applied Polymer Science, 124, 4782-4788.

[17]   Shen, H.B. and Nutt, S.R. (2003) Mechanical Characterization of Short Fiber Reinforced Phenolic Foam. Composites Part A: Applied Science and Manufacturing, 34, 899-906.
http://dx.doi.org/10.1016/S1359-835X(03)00136-2

[18]   Kiss, G. (1987) In Situ Composites: Blends of Isotropic Polymers and Thermotropic Liquid Crystalline Polymers. Polymer Engineering & Science, 27, 410-423.
http://dx.doi.org/10.1002/pen.760270606

[19]   Champagne, M.F., Dumoulin, M.M., Utrack, L.A. and Szabo, J.P. (1996) Generation of Fibrillar Morphology in Blends of Block Copolyetheresteramide and Liquid Crystal Polyester. Polymer Engineering & Science, 36, 1636-1646.
http://dx.doi.org/10.1002/pen.10560

[20]   Qin, Y., Brydon, D.L., Mather, R.R. and Wardman, R.H. (1993) Fibres from Polypropylene and Liquid Crystal Polymer (LCP) Blends: 1. Effect of LCP Concentration. Polymer, 34, 1196-1201.
http://dx.doi.org/10.1016/0032-3861(93)90772-3

[21]   Souza, J.P.D. and Baird, D.G. (1996) In Situ Composites Based on Blends of a Poly(ether imide) and Thermotropic Liquid Crystalline Polymers under Injection Moulding Conditions. Polymer, 37, 1985-1997.
http://dx.doi.org/10.1016/0032-3861(96)87317-4

[22]   Wei, C., Zeng, M., Xiong, X.M. and Zhang, F.A. (2010) Thermal and Frictional Properties of Modified Sisal Fibre/Phenolic Resin Composites. Plastics, Rubber and Composites, 39, 61-66.
http://dx.doi.org/10.1179/174328910X12608851832452

[23]   Lu, S.R., Jiang, Y.M. and Wei, C. (2009) Preparation and Characterization of EP/SiO2 Hybrid Materials Containing PEG Flexible Chain. Journal of Materials Science, 44, 4047-4055.
http://dx.doi.org/10.1007/s10853-009-3584-7

[24]   Mu, Q.H., Wei, C. and Feng, S.Y. (2009) Studies on Mechanical Properties of Sisal Fiber/Phenol Formaldehyde Resin In-Situ Composites. Polymer Composites, 30, 131-137.
http://dx.doi.org/10.1002/pc.20529

[25]   Yu, X.B., Wei, C., Xu, D., Lu, C.H., Yu, J.H. and Lu, S.R. (2007) Wear and Mechanical Properties of Reactive Thermotropic Liquid Crystalline Polymer/Unsaturated Polyester/Glass Fiber Hybrid Composites. Journal of Applied Polymer Science, 103, 3899-3906.
http://dx.doi.org/10.1002/app.25593

[26]   Verdejo, R., Barroso-Bujans, F. and Rodriguez-Perez, M.A. (2008) Functionalized Graphene Sheet Filled Silicone Foam Nanocomposites. Journal of Materials Chemistry, 18, 2221-2226.
http://dx.doi.org/10.1039/b718289a

[27]   Schniepp, H.C., Li, J.L., McAllister, M.J., Sai, H., Herrera Alonso, M., Adamson, D.H., et al. (2006) Functionalized Single Graphene Sheets Derived from Splitting Graphite Oxide. The Journal of Physical Chemistry B, 110, 8535-8539.
http://dx.doi.org/10.1021/jp060936f

[28]   Tan, S.T., Zhang, H.L. and Wang, X.Y. (1998) Chinese Journal of Polymer Science, 2, 167-171.

[29]   Kumar, N.A., Choi, H.J., Shin, Y.R., Chang, D.W., Dai, L.M. and Baek, J.B. (2012) Polyaniline-Grafted Reduced Graphene Oxide for Efficient Electrochemical Supercapacitors. ACS Nano, 6, 1715-1723.

 
 
Top