Erosion Behavior of AISI 6061-T6
ABSTRACT
In this work, erosion tests were performed to study the behavior of an aluminium alloy known as AISI 6061-T6 against the impact action of aluminium oxide abrasive particles. This material was selected because of its high ductility and tenacity. An erosion rig based on that in ASTM G76-95 was used to conduct the tests. The alumina particles had a particle size between 300 and 400 μm. Four incident angles, 30&deg, 45&deg, 60&deg and 90&deg were used to conduct the erosion tests. The particle velocity and the abrasive flow rate were 24 ± 2 m/s and 63 ± 0.5 g/min. The room temperature was between 35&degC and 40&degC. Chemical analysis of the material and abrasive particles were obtained using energy dispersive X-ray analysis (EDS). SEM images were employed to identify the wear mechanisms, which were characterized by high plastic deformation. The erosion rates were obtained and the results indicated that the maximum erosion damage was achieved at 30&deg reducing progressively at normal incidence.

Cite this paper
Laguna-Camacho, J. , Martínez-García, H. , Escamilla-Rodríguez, F. , Alarcón-Rosas, C. , Calderón-Ramón, C. , Ríos-Velasco, L. , Ríos-Velasco, L. , Pelcastre-Lozano, M. , Casados-Sánchez, Á. and González-Gómez, M. (2015) Erosion Behavior of AISI 6061-T6. Journal of Surface Engineered Materials and Advanced Technology, 5, 136-146. doi: 10.4236/jsemat.2015.53015.
References
[1]   Budinski, K.G. (1995) Erosion of 316 Stainless Steel by Dicalcium Phosphate. Wear, 186-187, 145-149.
http://dx.doi.org/10.1016/0043-1648(95)07165-2

[2]   Macchini, R., Bradley, M.S.A. and Deng, T. (2013) Influence of Particle Size, Density, Particle Concentration on Bend Erosive Wear in Pneumatic Conveyors. Wear, 303, 21-29.
http://dx.doi.org/10.1016/j.wear.2013.02.014

[3]   Akbarzadeh, E., Elsaadawy, E., Sherik, A.M., Spelt, J.K. and Papini, M. (2012) The Solid Particle Erosion of 12 Metals Using Magnetite Erodent. Wear, 282-283, 40-51.
http://dx.doi.org/10.1016/j.wear.2012.01.021

[4]   Azevedo, C.R.F. and Sinátora, A. (2009) Erosion Fatigue of Steam Turbine Blades. Engineering Failure Analysis, 16, 2290-2303.
http://dx.doi.org/10.1016/j.engfailanal.2009.03.007

[5]   Christman, T. and Shewmon, P.G. (1979) Erosion of a Strong Aluminium Alloy. Wear, 52, 57-70.
http://dx.doi.org/10.1016/0043-1648(79)90196-0

[6]   Cousens, A.K. and Hutchings, I.M. (1983) A Critical Study of the Erosion of an Aluminium Alloy by Solid Spherical Particles at Normal Impingement. Wear, 88, 335-348.
http://dx.doi.org/10.1016/0043-1648(83)90302-2

[7]   Veerabhadra-Rao, P., Young, S.G. and Buckley, D.H. (1983) Morphology of Ductile Metals Eroded by a Jet of Spherical Particles Impinging at Normal Incidence. Wear, 85, 223-237.
http://dx.doi.org/10.1016/0043-1648(83)90066-2

[8]   Feng, Z. and Ball, A. (1999) The Erosion of Four Materials Using Seven Erodents—Towards an Understanding. Wear, 233-235, 674-684.
http://dx.doi.org/10.1016/S0043-1648(99)00176-3

[9]   (1995) ASTM Standard, G76-95, Standard Practice for Conducting Erosion Tests by Solid Particle Impingement Using Gas Jets. Vol. 0.302, ASTM, Philadelphia, in Annual Book of ASTM Standards.

[10]   Kosel, T.H. and Anand, K. (1989) Optoelectronic Velocimeter Development (Technical Report). Technical Information Center, Oak Ridge.

[11]   Hutchings, I.M. and Winter, R.E. (1974) Particle Erosion of Ductile Metals: A Mechanism of Material Removal. Wear, 27, 121-128.
http://dx.doi.org/10.1016/0043-1648(74)90091-X

[12]   Tilly, G.P. (1969) Erosion Caused by Airborne Particles. Wear, 14, 63-79.
http://dx.doi.org/10.1016/0043-1648(69)90035-0

[13]   Finnie, I. (1960) Erosion of Surfaces by Solid Particles. Wear, 3, 87-103.
http://dx.doi.org/10.1016/0043-1648(60)90055-7

[14]   Harsha, A.P. and Kumar-Bhaskar, D. (2008) Solid Particle Erosion Behaviour of Ferrous and Non-Ferrous Materials and Correlation of Erosion Data with Erosion Models. Materials and Design, 29, 1745-1754.
http://dx.doi.org/10.1016/j.matdes.2008.03.016

[15]   Oka, Y.I., Nishimura, M., Nagahashi, K. and Matsumura, M. (2001) Control and Evaluation of Particle Impact Conditions in a Sand Erosion Test Facility. Wear, 250, 736-743.
http://dx.doi.org/10.1016/S0043-1648(01)00710-4

 
 
Top