Fatigue Limit Prediction and Estimation for the Crack Size Rendered Harmless by Peening for Welded Joint Containing a Surface Crack
ABSTRACT
In this study, the effects of portable pneumatic needle-peening (PPP) on the bending fatigue limit of a low-carbon steel SM490A welded joint containing a semi-circular slit on the weld toe were investigated. PPP was applied to the specimens with a semi-circular slit with depths of a = 0.4, 0.8, 1.2, and 1.6 mm. Then, three-point bending fatigue tests were carried out under R = 0.05. The fatigue limits of low-carbon steel welded specimens containing a semi-circular slit were increased for peened specimens compared with non-peened specimens. Peened specimens having a semicircular slit with a depth of a = 1.2 mm had high fatigue limits, almost equal to those of the non-slit peened specimens. It was concluded that a semi-circular slit with a depth of less than a = 1.2 mm can be rendered harmless by peening. Then, the fatigue improvement by peening was predicted. The fatigue limits before and after peening could be estimated accurately by using a modified Goodman diagram considering the effects of residual stress, stress concentration, and Vickers hardness. Moreover, the maximum depth of a semi-circular slit that can be rendered harmless by PPP was estimated based on fracture mechanics assuming that the semi-circular slit was equivalent to a semi-circular crack. The prediction results were almost consistent with the experimental results.

Cite this paper
Fueki, R. , Takahashi, K. and Houjou, K. (2015) Fatigue Limit Prediction and Estimation for the Crack Size Rendered Harmless by Peening for Welded Joint Containing a Surface Crack. Materials Sciences and Applications, 6, 500-510. doi: 10.4236/msa.2015.66053.
References
[1]   Takahashi, K., Amano, T., Hanaori, K., Ando, K. and Takahashi, F. (2009) Improvement of Fatigue Limit by Shot Peening for High-strength Steel Specimens Containing a Crack-like Surface Defect. Journal of the Society of Materials Science, Japan, 58, 1030-1036.
http://dx.doi.org/10.2472/jsms.58.1030

[2]   Houjou, K., Takahashi, K. and Ando, K. (2013) Improvement of Fatigue Limit by Shot Peening for High-Tensile Strength Steel Containing a Crack in the Stress Concentration Zone. International Journal of Structural Integrity, 4, 258-266.
http://dx.doi.org/10.1108/17579861311321726

[3]   Nose, T. and Shimanuki, H. (2008) Experiment and Analysis of Influence of Ultrasonic Peening on Fatigue Life in Pad Welded Joint. Transactions of the JSME Series A, 74, 166-168.
http://dx.doi.org/10.1299/kikaia.74.166

[4]   Togasaki, Y., Tsuji, H., Honda, T., Sasaki, T. and Yamaguchi, A. (2010) Effect of UIT on Fatigue Life in Web-Gusset Welded Joints. Journal of Solid Mechanics and Materials Engineering, 4, 391-400.
http://dx.doi.org/10.1299/jmmp.4.391

[5]   Marquis, G. (2010) Failure Modes and Fatigue Strength of Improved HSS Welds. Engineering Fracture Mechanics, 77, 2051-2062.
http://dx.doi.org/10.1016/j.engfracmech.2010.03.034

[6]   Houjou, K., Takahashi, K., Ando, K. and Abe, H., (2014) Effect of Peening on the Fatigue Limit of Welded Structural Steel with Surface Crack, and Rendering the Crack Harmless. International Journal of Structural Integrity, 5, 279-289.
http://dx.doi.org/10.1108/IJSI-12-2013-0048

[7]   Takahashi, K., Houjou, K., Abe, H., Ando, K. and Okazaki, S. (2013) Improvement of Structural Integrity of Pressure Vessels by Peening. Journal of Japan Boiler Association, 381, 15-22.

[8]   Ministry of Land, Infrastructure, Transport and Tourism (2012) New Technology Information System No. CB-120011-A.
http://www.netis.mlit.go.jp

[9]   Nose, T. (2012) Ultrasonic Peening Method for Fatigue Strength Improvement. Journal of the JWS, 77, 194-199.

[10]   Nishijima, S., Ishii, A., Kanazawa, K., Matsuoka, S. and Masuda, C. (1989) Collection of NRIM Fatigue Data Sheet. National Research Institute for Metals, No. 5, 39, 40, 54.

[11]   El Haddad, M.H., Topper, T.H. and Smith, K.N. (1979) Relation between Shot-Peening Residual Stress Distribution and Fatigue Crack Propagation Life in Spring Steel. Engineering Fracture Mechanics, 11, 573-584.
http://dx.doi.org/10.1016/0013-7944(79)90081-X

[12]   Tange, A. Akutu, T. and Takamura, A. (1991) Improvement of Fatigue Limit by Shot Peening for High-Strength Steel Specimens Containing a Crack-Like Surface Defect. Transactions of JSSE, No. 36, 47-53.

[13]   National Research Institute for Metals (1980) NRIM Fatigue Data Sheet. National Research Institute for Metals, Tokyo, No. 21, 11.

[14]   Newman Jr., J.C. and Raju, I.S. (1981) An Empirical Stress-Intensity Factor Equation for the Surface Crack. Engineering Fracture Mechanics, 15, 185-192.
http://dx.doi.org/10.1016/0013-7944(81)90116-8

 
 
Top