Investigating the Preparation Conditions on Superconducting Properties of Bi2-x LixPb0.3Sr2Ca2Cu3O10+δ
ABSTRACT
One and multi-step solid state reaction methods were used to prepare a high temperature superconductor with a nominal compositionBi2-x LixPb0.3Sr2Ca2Cu3O10+δ for ( 0 ≤ x ≤ 0 .5). T he effect o f preparation conditions and substituting Li on Bi sites had been investigated by the use of X-ray diffraction, resistance measurements and oxygen content to obtain the optimum conditions for formation and stabilization of the 2223-phase. It has been found that intermediate grinding will force to convert and accelerate the formation rate of the 2223-phase. The morphological analyses were carried out by SEM. The results showed that the multi-step technique was appropriate to prepare the compositio Bi2-x LixPb0.3Sr2Ca2Cu3O10+δ . X-ray diffraction analysis showed two phases: high-TC phase 2223 and low-TC phase 2212 with orthorhombic structure for all samples. However, the optimum concentration was found for 0.3 which improved the microstructure and had the highest TC  value 130 K for the highest value of oxygen content.

Cite this paper
Abbas, M. , Oboudi, S. and Raoof, N. (2015) Investigating the Preparation Conditions on Superconducting Properties of Bi2-x LixPb0.3Sr2Ca2Cu3O10+δ. Materials Sciences and Applications, 6, 310-321. doi: 10.4236/msa.2015.64036.
References
[1]   Saleh, S.A. (2006) Studies on Sintering Effect on the Structural and Transport Properties of (2223) Phase. Physica C, 444, 40-44.
http://dx.doi.org/10.1016/j.physc.2006.05.101

[2]   Muhammad, A.R. and Maqsood, A. (2010) Synthesis and Thermo Physical Characterization of Bismuth Based High-Tc Superconductors, Superconductor.
http://www.intechopen.com/books/superconductor/synthesis-and-thermophysical-characterization-of-bismuth-based-high-tc-superconductors

[3]   Takano, M., Takada, J., Oda, K., Kitaguchi, H., Miura, Y., Ikeda, Y., Tomii, Y. and Mazaki, H. (1988) High-TC Phase Promoted and Stabilized in the Bi, Pb-Sr-Ca-Cu-O System. Japanese Journal of Applied Physics, 27, L1041-L1043.
http://dx.doi.org/10.1143/JJAP.27.L1041

[4]   Agostinelli, E., Bohandy, J., Green, W.J., Bargeron, C.B., Phillips, T.E., Kim, B.F., Adrian, F.J. and Moorjani, K. (1989) Stabilization of the 108 K Superconducting Phase in the Bi0.7Pb0.3SrCaCu1.8Oy System. Journal of Superconductivity, 2, 3361-367.
http://dx.doi.org/10.1007/BF00618523

[5]   Dey, T.K. (1998) Effect of Sintering Duration on the Thermal Conductivity of (Bi, Pb)-2223 Superconducting Pellets between 10 and 150 K. Journal of Superconductivity, 11, 279-284. http://dx.doi.org/10.1023/A:1022692119723

[6]   Fernando, P.R. and Pathmanathan, N. (2006) Fabrication and Characterization of Bi1.6Pb0.4Sr2Ca2Cu3Oy Superconductors Prepared by Solid State Reaction Technique. Sri Lankan Journal of Physics, 7, 7-13.

[7]   Bilgili, O., Selamet, Y. and Kocabas, K. (2008) Effects of Li Substitution in Bi-2223 Superconductors. Journal of Superconductivity and Novel Magnetism, 21, 439-449.
http://dx.doi.org/10.1007/s10948-008-0374-4

[8]   Abbas, M.M., Abass, L.K. and Salman, U. (2012) Influences of Sintering Time on the TC of Bi2-xCuxPb0.3Sr2Ca2Cu3O10+Δ High Temperature Superconductors. Energy Procedia, 18, 215-224. http://dx.doi.org/10.1016/j.egypro.2012.05.033

[9]   Koyama, S., Endo, U. and Kawai, T. (1988) Preparation of Single 110 K Phase of the Bi-Pb-Sr-Ca-Cu-O Superconductor. Japanese Journal of Applied Physics, 27, L1861-L1863.
http://dx.doi.org/10.1143/JJAP.27.L1861

[10]   Kocabas, K. (1998) Effect of Sintering Time on Sb Added BiPbSrCaCuO Superconducting Ceramics. Turkish Journal of Physics, 22, 437-440.

[11]   Gundakaram, R., Chang, S.C., Liu, R.S., Woodall, L. and Gerards, M. (2001) Studies into the Phase Transformation of Bi-2223 Precursor Powders Using X-Ray Diffraction and SQUID Susceptibility Measurements. IEEE Transactions on Applied Superconductivity, 11, 3182-3185.
http://dx.doi.org/10.1109/77.919739

[12]   Mohammed, N.H., Awad, R., Abou-Aly, A.I., Ibrahim, I.H. and Hassan, M.S. (2012) Optimizing the Preparation Conditions of Bi-2223 Superconducting Phase Using PbO and PbO2. Journal of Materials Science and Applications, 3, 224-233.
http://dx.doi.org/10.4236/msa.2012.34033

[13]   Azhan, H., Azman, K. and Yusainee, S.Y.S. (2009) The Role of Antimony (Sb) Addition on BSCCO Superconductor. Solid State Science and Technology, 17, 215-221.

[14]   lkeda, Y., Takno, M., Hiroi, Z., Oda, K., Kitaguchi, H., Takada, J., Miura, Y., Takada, Y., Yamamoto, O. and Mazaki, H. (1988) The High-Tc with a New Modulation Mode in the Bi,Pb-Sr-Ca-Cu-O System. Japanese Journal of Applied Physics, 27, L2067-L2070.
http://dx.doi.org/10.1143/JJAP.27.L2067

[15]   Bolat, S., Yanmaz, E. and Comert, H. (2000) Properties of Ag-Doped Bi1.6Pb0.4Sr2Ca3Cu4-xAgxOy (2234) Oxides Prepared by S.S.R. Method. Turkish Journal of Physics, 24, 129-135.

[16]   Iqbal, M.J. and Mehmood, R. (2009) Improvement in High-Tc Phase Formation in (Thallium-Antimony) Doped Bismuth-Based Superconducting Materials. Journal of Alloys and Compounds, 477, 386-390.
http://dx.doi.org/10.1016/j.jallcom.2008.10.006

[17]   Heh, T.S., Chen, J.R. and Tseng, T.Y. (1990) Preparation of Bi0.7Pb0.3SrCaCu1.8Oy High-Tc Superconductor by the Citrate Method. Japanese Journal of Applied Physics, 29, 4652-4655.

[18]   Halim, S.A., Ravandi, S.S.H., Adam, M.I., Chen, S.K., Lim, K.P., Baqiah, H., Faisal, M.A.M. and Kamarulzaman, M.M. (2010) Influence of Addition of Eu2O3 Nanoparticle on the Structural and Superconducting Properties of (Bi1.6Pb0.4)Sr2Ca2Cu3O10 Ceramics. Solid State Science and Technology, 18, 266-271.

[19]   Fujii, T., Terasaki, I., Watanabe, T. and Matsuda, A. (2002) Doping Dependence of Anisotropic Resistivities in Trilayered Superconductor Bi2Sr2Ca2Cu3O10+δ (Bi-2223). Physical Review B, 66, Article ID: 024507.

[20]   Parinov, I.A. (2012) Microstructure and Properties of High-Temperature Superconductors. Springer-Verlag Berlin Heidelberg, Berlin.
http://dx.doi.org/10.1007/978-3-642-34441-1

[21]   Mihalache, V., Aldica, G. and Miu, D. (2006) Modification of the Superconducting Parameters of Bi-Sr-Ca-Cu-O by Iodine Intercalation. Journal of Optoelectronics and Advanced Materials, 8, 1287-1291.

[22]   Hermiz, G. (2001) Thermal Analysis and Phase Transformation of HTSC of (Bi1-xPbx)2(Sr1-yBay)2Ca2Cu3O10 Compound. Ph.D. Thesis, Baghdad University, Baghdad.

[23]   McKernan, S. and Zettl, A. (1993) High-Temperature Resistivity and Oxygen Diffusion in Bi2Sr2CaCuOx. Physics C, 209, 585-590.
http://dx.doi.org/10.1016/0921-4534(93)90579-F

[24]   Al-Taie, S. (2004) Investigation of Preparation Process and Composition of the Superconductor Bi1.6Pb0.4Sr2+xCa2+yCu3 O10+a. Master’s Thesis, Baghdad University, Baghdad.

[25]   Mua, N.T., Sundaresan, A., Man, N.K. and Dung, D. (2014) Influence of Preparation Conditions on Superconducting Properties of Bi-2223 Thin Films. Bulletin of Materials Science, 37, 19-25.
http://dx.doi.org/10.1007/s12034-014-0627-8

[26]   Zhao, J., Wu, M., Abdul-Razzaq, W. and Seehra, M.S. (1990) Interrelationship between the Transition Temperatures of the (2223) and (2212) Phases of Bi-Based Superconductors. Physica C, 165, 135-138.
http://dx.doi.org/10.1016/0921-4534(90)90156-9

[27]   Khaled, J., Komatsu, T. and Sato, R. (1997) Formation and Thermal Stability of High-Tc Phase in Te-Doped Bi-Based Superconducting Glass-Ceramics. Journal of the Ceramic Society of Japan, 105, 279-283.
http://dx.doi.org/10.2109/jcersj.105.279

[28]   Maeda, H. and Togano, K. (1996) Bismuth-Based High Temperature Superconductors. Marcel Dekker, Inc., New York.

[29]   Shatkovskis, E., Dapkus, L. and Pyragas, V. (2000) The Metastable Superior Phases in Bi-2212 Perovskite-Like High- Temperature Superconductor. Defects and Surface-Induced Effects in Advanced Perovskites: NATO Science Series, 77, 161-166.
http://dx.doi.org/10.1007/978-94-011-4030-0_17

 
 
Top