JMMCE  Vol.3 No.3 , May 2015
Age Strengthening of Grey Cast Iron Alloys for Machine Cutting Tools Production
ABSTRACT
This work was carried out with the aim of using alloying and ageing processes to develop new alloys from grey cast iron that will have optimum properties suitable for the manufacturing of machine cutting tools. Four different alloys of grey cast iron with alloying composition of Fe-3% Al-2.5% Cr-2% Mo; Fe-3% Al-2% Cr-2% Mo; Fe-3% Al-2.5% Cr-1.5% Mo and Fe-3% Al-1.5% Cr-2% Mo were produced. The chemical analysis of both as-received base metal and produced alloys was determined using Spetro-CJRO Arc-Spectrometer. The microstructural properties and mechanical properties (hardness, impact toughness and ultimate tensile strength) of the produced alloys were determined for both as-cast samples and aged samples. The results showed that the addition of these alloying elements slightly decreased carbon, silicon and phosphorus content and thereby changed the hypereutectic cast iron to hypoeutectic by reducing the carbon equivalent. Also the morphology of graphite flake was changed as a result of the formation of nitrides and carbides of different phases. The results of the mechanical properties showed that the maximum hardness values obtained for each of the four alloys produced and aged at 300?C are 71.5 HRc, 69 HRc, 66.5 HRc and 65.4 HRc respectively. The maximum values for impact toughness obtained for each of the same produced alloys are 66 J, 63.6 J, 62 J and 60.3 J respectively. Also the maximum ultimate tensile strength values obtained for each of the alloys are 1380 N·mm-2, 1311 N·mm-2, 1260 N·mm-2 and 1190 N·mm-2. Comparing the properties obtained from the produced alloys with those of the commercial cutting tools, it was found that cutting tools manufactured from these produced alloys can compete favourably with cast cobalt tool, high speed steel (HSS) and tool steel.

Cite this paper
Opaluwa, A. , Oyetunji, A. and Seidu, S. (2015) Age Strengthening of Grey Cast Iron Alloys for Machine Cutting Tools Production. Journal of Minerals and Materials Characterization and Engineering, 3, 107-117. doi: 10.4236/jmmce.2015.33013.
References
[1]   Callister, W.D. (2000) Fundamentals of Materials Science and Engineering. John Wiley & Sons Inc., New York, 69- 185.

[2]   Jain, R.K. (2008) Production Technology. Khanna Publishers, NaiSarak, Delhi, 138-244.

[3]   Agarwal, R.I., Banga, T.R. and Tahil, M. (2007) Foundry Engineering. Hanna Publishers, New Delhi, 22-56.

[4]   Edington, V.E., Richards, V.L. and Nicola, W. (2002) Age Strengthening of Gray Cast Iron: Nitrogen Effects and Machinability. AFS Transactions, 120, 983 - 994.

[5]   Malinov, S., Bottger, A.J., Mittemeijer, E.J. and Somers, M.A.J. (2001) Phase Transformations and Phase Equilibria in the Fe-N System at Temperatures below 573 K. Metallurgical and Materials Transactions, 32, 59-73.
http://dx.doi.org/10.1007/s11661-001-0102-1

[6]   Richards, V.L., Aken, D.C. and Nicola, W.M. (2000) Age Strengthening of Gray Cast Iron Phase II: Nitrogen and Melting Method Effects. AFS Transactions, 127, 233-238.

[7]   Mahran, M. (2007) The Tendency of the Different Alloying Elements to form Hard Nitrides of the Iron by a Mechanism Known as Precipitation Hardening. Christian Doppler Laboratory, 1-15.

[8]   Anish, T.V. (2002) Age Strengthening of Gray Cast Iron: Alloying Effects and Kinetic Study. AFS Transactions, 120, 995-1002.

[9]   Aken, D.C., Richards, V.L. and Nicola, W. (2003) Age Strengthening of Gray Cast Iron: Kinetics Study. AFS Transactions, 303, 98-108

[10]   Khanna, O.P. (2009) Materials Science and Metallurgy. Dhanpat Rail Publication Limited, New Delhi, 1-17.

[11]   Marinov, V. (2007) Cutting Tool Requirements. Manufacturing Technology. Pearson Prentice Hall, Upper Saddle River.

[12]   Soiński, M.S. and Góraj, J. (2009) The Influence of Cerium Mixture Addition on the Structure of Cast Iron Containing about 5% Aluminium. Archives of Foundry Engineering, 9, 215-218.

[13]   Zió?kowskia, E. and Wrona, R. (2007) Using Fuzzy Optimization Method in Calculation of Charge Burden to Correct the Chemical Composition of Metal Melt. Archives of Foundry Engineering, 7, 183-186.

[14]   Hurtalova, I., Lilova, E., Chalupova, M. and Durimikova, I. (2013) Effect of Chemical Composition of Secondary Al-Si Cast Iron Alloys on Intermetallic Phases. Elservier. www.elservier.com

[15]   Youping, M.A., Xlulan, L.J., Yugoa, L.I.U. and Xlaoving, D. (2013) Microstructures and Properties of Ti-Nb-V-Mo Alloyed High Chromium Cast Iron. Bulletin of Materials Science, 36, 839-844.
http://dx.doi.org/10.1007/s12034-013-0558-9

[16]   Kalpakjian, S. (2006) Manufacturing Engineering and Technology. Pearson Education Inc., Pearson Prentice Hall, Upper Saddle River, 275-340.

[17]   Luyckx, S. and Love, A. (2010) The Relationship between the Abrasion Resistance and the Hardness of WC-Coating. Elservier. www.elservier.com/locate/wear

[18]   Harry, C. (1999) Hardness Testing. ASM International. www.asminternational.org

[19]   Jamino, M.R. (2013) Metallography and Microstructures of Cast Iron. ASM International Hand Book, 9, 99-104.

[20]   Smallman, R.E. (1990) Modern Physical Metallurgy. Butterworth and Co. Ltd., London.

 
 
Top