Study of Deformation Coating for Sheets by Using Tensile Test
ABSTRACT
This article focuses on the study of the defined values of tensile strain and the effect of low temperature plasma adhesion selected coatings on steel samples using a tensile testing flat test bars. Samples were made by machining and welding technologies. The flat test bars were tested by pulling on a test rig UPC 1200. Part of the samples was treated on the surface prior to coating by a tensile test, second base coat and with a final coat continuous multi plasma system. The selected test samples were determined from the tensile test of the material characteristics apparent from the tensile diagrams. The examined samples were fitted top and base coat. Another group was the KTL basis. The presented graphs show the dependence of the strength on elongation of a sample according to DIN EN ISO 6892-2. The samples were then examined under a stereo microscope SCHUT brand, type SSM-E in the laboratory to conduct coating on a steel sheet at the moment of total violation sectional samples. The base layer, in which the temperature ranges from 160°C - 180°C, was applied by electrophoresis method.

Cite this paper
Dvořák, M. , Schwarzer, E. and Klíma, M. (2015) Study of Deformation Coating for Sheets by Using Tensile Test. Journal of Surface Engineered Materials and Advanced Technology, 5, 73-83. doi: 10.4236/jsemat.2015.52008.
References
[1]   Hermann, F. and Schiller, M. (2007) Testing of Paints and Protective Coatings. Pardubice-Green Suburb: SYNPO PLC.

[2]   Test of Resistance of Coatings (2004) Measuring Equipment, Thickness, Hardness, Gloss Meters, Thermometers. Pro- Inex Instruments, Ltd., Ostrava.

[3]   Dvorák, M., et al. (2001) Technology II. Academic Publishing CERM, Ltd., Brno, 236-238.

[4]   CSN EN ISO 1519 (2002) Paints Substance—Bend Test (Cylindrical Mandrel). Czech Standards Institute.

[5]   CSN EN ISO 7438 (2005) Metallic Materials Bend Test. Czech Standards Institute, 11-12.

[6]   CSN ISO 24213 (2009) Metallic Materials—Sheets and Belt: Evaluation Method of Suspension for Flexural Bending. Czech Standards Institute, 14-15.

[7]   Blanks, T. (1985) Metals Handbook: Mechanical Testing. American Society for Metals, 837-842.

[8]   Cada, R. (1998) Surface Formability of Metallic Materials. Technical University of Ostrava, Ostrava, 90-92.

[9]   CSN EN ISO 20482 (2004) Metallic Materials-Sheet and Belts-Bulge Tests According to Erichsen. Czech Standards Institute, Prague.

[10]   CSN EN 13144 (2003) Metallic and Other Inorganic Coatings: Method for Quantitative Measurement of Adhesion for Tensile Test. Czech Standards Institute, 12-13.

[11]   Dvorák, M. and Schwarzer, E. (2013) Study of Formability of Coated Sheets from the Plasma Chemical Pretreatment of Surfaces. International Journal of Engineering and Innovative Technology (IJEIT), 3, 356-360.

[12]   Patent EP 1077021, US 6,525,481 (2005) Method of Making a Physically and Chemically active Environment by Means of Plasma Jet and the Related Plasma JET. Masaryk University, Brno, 5-6.

[13]   Krejcík, V. (1988) Surface Treatment of Metals II. Publishing House of Technical Literature, Prague.

[14]   Kraus, V. (2000) Surface Modification. University of West Bohemia, Plzeň, 218-220.

[15]   Kreibich, V. (1996) Theory and Technology of Surface Treatment. Publishing House of CVUT, Prague, 89-92.

[16]   Forejt, M. and Píska, M. (2006) Theory of Machining, Molding and Tool. CERM, Academic Publishing, Ltd., Brno, 225-226.

[17]   Husek, M. and Dvorák, M. (2010) Test of Adherence Multifunctional Coating on the Sheet Using a Graduated Bending Jig. Engineering Technology, 15, 15-20.

[18]   Dvorák, M. and Schwarzer, E. (2012) New Methods Testing of Adhesion of the Coating to Sheet Metal by Bending. Journal of Surface Engineered Materials and Advanced Technology (JSEMAT), 2, 61-64.

 
 
Top