MSA  Vol.6 No.3 , March 2015
Characterization of Low Cost Ion Conducting Poly(AAc-co-DMAPMA) Membrane for Fuel Cell Application
ABSTRACT
Poly(AAc-co-DMAPMA) membrane (PADMA) is synthesized by free radical aqueous copolymerization of acrylic acid (AAc) and N-3-[dimethylamino)propyl]-methacrylamide (DMAPMA) to check its stability and conductivity. The hydrogel membrane characterized physically to study morphology by SEM, thermal stability by TGA and mechanical stability by measuring compressive strength and ionic conductivity by electrochemical impedance spectroscopy in alkaline as well as in acidic environment at different temperatures. The compression modulus of the hydrogel membrane is 24 kPa at pH = 1.0 and 16 kPa at pH = 7.0, and stable (no fracture) till 72% deformation. The PADMA hydrogel membrane ionic conductivity increased with the increase in temperature and structurally stable up to 190°C. Improvement in ionic conductivity is observed after the heat treatment of the membrane. Compared with ionic conductivity of Nafion? (SE512), the PADMA membrane found to be inferior. However, the PADMA hydrogel membrane conductivity was greater (~1 × 10-4S/cm) at low and high pH compared with neutral pH (~1 × 10-5S/cm) indicating the possibility of using the membrane as either a proton and hydroxyl ion conductor.

Cite this paper
Das, A. , Basu, S. , Verma, A. and Scott, K. (2015) Characterization of Low Cost Ion Conducting Poly(AAc-co-DMAPMA) Membrane for Fuel Cell Application. Materials Sciences and Applications, 6, 234-241. doi: 10.4236/msa.2015.63028.
References
[1]   Dhathathreyan, K.S. and Rajalaxmi, N. (2007) Polymer Electrolyte Membrane Fuel Cell. In: Basu, S., Ed., Recent Trends in Fuel Cell Science and Technology, Springer, New York, 40-115.
http://dx.doi.org/10.1007/978-0-387-68815-2_3

[2]   Kamarudin, S.K., Daud, W.R.W., Som, A.Md., Takriff, M.S. and Mohammad, A.W. (2006) Technical Design and Economic Evaluation of a PEM Fuel Cell System. Journal of Power Sources, 157, 641-649.
http://dx.doi.org/10.1016/j.jpowsour.2005.10.053

[3]   Lobato, J., Canizares, P., Rodrigo, M.A., Linares, J.J., Aguilar, J.A. (2007) Improved Polybenzimidazole Films for H3PO4-Doped PBi-Based High Temperature PEMFC. Journal of Membrane Science, 306, 47-55.
http://dx.doi.org/10.1016/j.memsci.2007.08.028

[4]   Scott, K., Pilditch, S. and Mamlouk, M. (2007) Modelling and Experimental Validation of a High Temperature Polymer Electrolyte Fuel Cell. Journal of Applied Electrochemistry, 37, 1245-1259.
http://dx.doi.org/10.1007/s10800-007-9414-1

[5]   Li, M., Shao Z. and Scott, K. (2008) A High Conductivity Cs2.5H0.5PMo12O40/Polybenzimidazole (PBI)/H3PO4 Com- posite Membrane for Proton-Exchange Membrane Fuel Cells Operating at High Temperature. Journal of Power Sour- ces, 183, 69-75.
http://dx.doi.org/10.1007/s10800-007-9414-1

[6]   Nikolic, V.M., Kekljes, A., Popovic, Z.K., Lausevic, Z.V. and Miljanic, S.S. (2007) On the Use of Gamma Irradiation Crosslinked PVA Membranes in Hydrogen Fuel Cells. Electrochemistry Communications, 9, 2661-2665.
http://dx.doi.org/10.1016/j.elecom.2007.08.022

[7]   Kim, W.J., Choi, H.G., Lee, Y.K., Nam, J.D., Cho, S.M. and Chung, C.H. (2006) Hydrogels in Methanol Fuel Car- tridge Used as a Diffusion-Rate-Controlling Agent Suppressing the Methanol Crossover in Passively Operated Flat- Pack Type DMFCs. Journal of Power Sources, 157, 193-195. http://dx.doi.org/10.1016/j.jpowsour.2005.07.033

[8]   Das, A. and Ray, A.R. (2008) Synthesis and Characterization of Poly(acrylic acid-co-N-[3-(dimethylamino)propyl]- methacrylamide) Hydrogel Membranes for Biomedical Applications. Journal of Applied Polymer Science, 108, 1273- 1280.
http://dx.doi.org/10.1002/app.27665

[9]   Muniz, E.C. and Geuskens, G. (2001) Compressive Elastic Modulus of Polyacrylamide Hydrogels and Semi-IPNs with Poly(N-isopropylacrylamide. Macromolecules, 34, 4480-4484.
http://dx.doi.org/10.1021/ma001192l

[10]   Verma, A. and Scott, K. (2010) Development of High Temperature PEMFC Based on Heteropolyacids and Polyben- zimidazole. Journal of Solid State Electrochemistry, 14, 213-219.
http://dx.doi.org/10.1007/s10008-008-0678-0

[11]   Robinson, R.A. and Stokes, R.H. (1968) Electrolyte Solutions. 2nd Edition, Butterworths, London.

[12]   Kawano, Y., Wang, R.A. and Palmer, S.R. (2002) Stress-Strain Curve of Nafion Membranes. Polimeos: Ciencia e Tech- nologia, 12, 96-101.

[13]   Unlu, M., Zhou, J. and Kohl, P.A. (2009) Hybrid Anion and Proton Exchange Membrane Fuel Cells. The Journal of Physical Chemistry C, 113, 11416-11423.

[14]   Hickner, M.A., Tudryn, G.J., Alam, T.M., Hibbs, M.R. and Fujimoto, C.H. (2009) Polymers with Tethered Anionic and Cationic Groups as Membranes for Fuel Cells. Macromolecular Symposia, 279, 59-62.
http://dx.doi.org/10.1002/masy.200950509

[15]   Caykara, T., Demiray, M. and G?ven, O. (2005) Effect of Type and Concentration of Surfactants on Swelling Behavior of Poly[N-[3-(dimethylamino) propyl]methacrylamide-co-N,N-methylenebis (acrylamide)] Hydrogels. Colloid and Poly- mer Science, 284, 258-265.
http://dx.doi.org/10.1007/s00396-005-1365-7

 
 
Top