Semi-Quantitative Estimation of Ce3+/Ce4+ Ratio in YAG:Ce3+ Phosphor under Different Sintering Atmosphere
Abstract: In order to confirm the relationship between the luminescence and the ratio of Ce3+/Ce4+ more clearly, a series of YAG:Ce3+ (Yttrium Aluminum Garnet, Y2.94Al5O12:0.06Ce3+) phosphors were pre- pared under different sintering atmosphere. A semi-quantitative analysis based on X-ray photoe-lectron spectroscopy (XPS) was introduced to study the mole ratio of Ce3+/Ce4+ in the as-synthesized YAG:Ce3+ phosphors. The results indicated that the percentage of Ce3+/(Ce3+ + Ce4+) reached 88.46% under the reduction atmosphere. The emission intensity of YAG:Ce3+ phosphors was in-creased significantly with the increasing of Ce3+ concentration.
Cite this paper: Wang, L. , Zhuang, L. , Xin, H. , Huang, Y. and Wang, D. (2015) Semi-Quantitative Estimation of Ce3+/Ce4+ Ratio in YAG:Ce3+ Phosphor under Different Sintering Atmosphere. Open Journal of Inorganic Chemistry, 5, 12-18. doi: 10.4236/ojic.2015.51003.

[1]   Abi-Aad, E., Bechara, R., Grimblot, J., et al. (1993) Preparation and Characterization of CeO2 under an Oxidization Atmosphere. Thermal Analysis, XPS, and EPR Study. Chemistry of Materials, 5, 793-797.

[2]   Cabala, M., Veltruská, K. and Matolín, V. (2007) Adsorption Properties of Ce/Ag System. WDS’07 Proceedings of Contributed Papers, Part III, 134-139.

[3]   Chai, C.L., Yang, S.Y., Liu, Z.K., et al. (2003) Violet/Blue Photoluminescence from CeO2 Thin Film. Chinese Science Bulletin, 48, 1198-1200.

[4]   Zuo, Y., Li, L.P., Huang, X.S., et al. (2014) Ce0.9Fe0.1O1.97/Ag: A Cheaper Inverse Catalyst with Excellent Oxygen Storage Capacity and Improved Activity towards CO Oxidation. The Royal Society of Chemistry, 4, 402-410.

[5]   Mullins, D.R., Overbury, S.H. and Huntley, D.R. (1998) Electron Spectroscopy of Single Crystal and Polycrystalline Cerium Oxide Surfaces. Surface Science, 409, 307-319.

[6]   Yu, X.W., Yan, C.W., Cao, C.A., et al. (2003) XPS Analysis of the Cerium Conversion Coating on the Anodized Al6061/SiCp. Journal of Materials Science and Technology, 19, 157-160.

[7]   Wen, M.F., Yu, B., Wang, Q.P., et al. (2004) Study on the Properties of Nanometer CeO2 Doped with Zr4+, La3+, Pr3+. Journal of Materials Science and Technology, 20, 357-360.

[8]   Luo, L.Z., Wang, X.L., Fu, X.G., et al. (2004) Study on Surface and Bulk Properties of Ce-5% Lanthanum Alloy. Journal of Rare Earths, 22, 22-25.

[9]   Wang, P., Wang, D.-J., Song, J., et al. (2012) Incorporation of Si-O Induced Valence State Variation of Cerium Ion and Phase Evolution in YAG:Ce Phosphors for White Light Emitting Diodes. Journal of Materials Science: Materials Electronic, 23, 1764-1769.

[10]   Liu, S.H., Wang, D.H. and Pan, C.H. (1988) Analysis of X-Ray Photoelectron Spectroscopy. Science Press, 69.