Zr-Ti-Ni-Cu Amorphous Brazing Fillers Applied to Brazing Titanium TA2 and Q235 Steel
ABSTRACT
Ti-Zr-Cu-Ni amorphous filler with good performance is suitable for joining TC and TB titanium alloy, but its melting temperature is higher than 882.5°C, the αβ phase transition temperature of TA2, which makes the ductility of TA2 fall and the microstructure of the joint coarse. In this paper, Ti-Zr-Cu-Ni amorphous filler was redesigned and optimized by using orthogonal experiment to obtain three easy-to-use Zr-Ti-Ni-Cu amorphous fillers with low melting points and good plasticity. The fast cooling equipment was used to fabricate the brazing filler foils to implement the braze welding of TA2 and Q235 with high frequency inductance. The results indicate that all the brazing foils are amorphous structure with lower melting temperature, for example, Zr52Ti22Ni18Cu8 filler’s is 538°C. The technical parameters in brazing welding are: welding temperature T = 800°C; heating electric current I =25 A; heating time t = 15 s and holding time t = 15 s, in the case of these conditions, the jointing head shear strength of TA2/Zr52Ti24Ni13Cu11/Q235 is 139 MPa. Fracture is mainly located in the brazing seam. The white brittle intermetallic TiFe, TiFe2 and enhancement TiC spread in the center zone of brazing seam.

Cite this paper
Cui, J. , Zhai, Q. , Xu, J. , Wang, Y. and Ye, J. (2014) Zr-Ti-Ni-Cu Amorphous Brazing Fillers Applied to Brazing Titanium TA2 and Q235 Steel. Materials Sciences and Applications, 5, 823-829. doi: 10.4236/msa.2014.511082.
References
[1]   Onzawa, T., Suzumura, A. and Ko, M. (2011) Structure and Mechanical Properties of CP Ti and Ti-6Al-4V Alloy Joints Brazed with Ti-Based Amorphous Filler Metals. Journal of the Japan Welding Society, 5, 205-211.

[2]   Qi, Y., Zhang, Y.H. and Quan, B.Y. (2003) Development and Application of Braze Welding and Ti-Based Braze Material. Metallic Functional Materials, 10, 31-37.

[3]   Huang, Y.J., et al. (2008) Formation, Thermal Stability and Mechanical Properties of Ti42.5Zr7.5Cu40Ni5Sn5 Bulk Metallic Glass. Science in China Series G: Physics, Mechanics and Astronomy, 51, 372-378.
http://dx.doi.org/10.1007/s11433-008-0049-y

[4]   Shapiro, A.E. and Flom, Y.A. (2012) Brazing of Titanium at Temperature below 800°C: Review and Prospective Applications. Welding Journal, 50, 1-22.

[5]   Chang, H. and Luo, G.Z. (1995) Development of Ti Alloy Used Brazing Filler Metals. Rare Metal Materials and Engineering, 24, 15-20.

[6]   Zhang, Q.P. and Zhang Y.S. (2005) Technology and the Developmental Situation of the Titanium Alloy. Aerodynamic Missile Journal, 7, 56-64.

[7]   Takemoto, T. (1988) Intermetallic Compounds Formed during Brazing of Titanium with Aluminum Filler Metals. Journal of Material Science, 6, 1301-1308.
http://dx.doi.org/10.1007/BF01154593

[8]   Xu, J.F. and Wei, B.B. (2004) Liquid Phase Flow and Microstructure Formation during Rapid Solidification. Acta Physica Sinica, 53, 160-166.

[9]   Elrefaey, A. and Tillmann, W. (2007) Interface Characteristics and Mechanical Properties of the Vacuum-Brazed Joint of Titanium-Steel Having a Silver-Based Brazing Alloy. Metallurgical and Materials Transactions, 38, 2956-2961.
http://dx.doi.org/10.1007/s11661-007-9357-5

[10]   Zhai, Q.Y., Xu, J.F. and Cui, J. (2013) A Kind of Amorphous Brazing Fillers Applied to Brazing Series TA Titanium Alloy and Stainless Steel. The Chinese Patent No. ZL2013104891392.

 
 
Top