Toughness Improvement of Geothermal Well Cement at up to 300°C: Using Carbon Microfiber
Abstract: This study aimed at assessing the usefulness of carbon microfiber (CMF) in improving the compressive-toughness of sodium metasilicate-activated calcium aluminate/Class F fly ash foamed cement at hydrothermal temperatures of up to 300°C. When the CMFs came in contact with a pore solution of cement, their surfaces underwent alkali-caused oxidation, leading to the formation of metal (Na, Ca, Al)-complexed carboxylate groups. The extent of this oxidation was enhanced by the temperature increase, corresponding to the incorporation of more oxidation derivatives at higher temperatures. Although micro-probe examinations did not show any defects in the fibers, the enhanced oxidation engendered shrinkage of the interlayer spacing between the C-basal planes in CMFs, and a decline in their thermal stability. On the other hand, the complexed carboxylate groups present on the surfaces of oxidized fibers played a pivotal role in improving the adherence of fibers to the cement matrix. Such fiber/cement interfacial bonds contributed significantly to the excellent bridging effect of fibers, resistance to the cracks development and propagation, and to improvement of the post-crack material ductility. Consequently, the compressive toughness of the 85°-, 200°-, and 300°C-autoclaved foamed cements reinforced with 10 wt% CMF was 2.4-, 2.9-, and 3.1-fold higher than for cement without the reinforcement.
Cite this paper: Sugama, T. and Pyatina, T. (2014) Toughness Improvement of Geothermal Well Cement at up to 300°C: Using Carbon Microfiber. Open Journal of Composite Materials, 4, 177-190. doi: 10.4236/ojcm.2014.44020.

[1]   Gill, S., Pyatina, T. and Sugama, T. (2012) Thermal Shock-Resistant Cement. Geothermal Resources Council (GRC) Transactions, 36, 445-451.

[2]   Lau, A. and Anson, M. (2006) Effect of High Temperatures on High Performance Steel Fiber Reinforced Concrete. Cement and Concrete Research, 36, 1698-1707.

[3]   Banthia, N. and Sappakittipakorn, M. (2007) Toughness Enhancement in Steel Fiber Reinforced Concrete through Fiber Hybridization. Cement and Concrete Research, 37, 1366-1372.

[4]   Abrishambaf, A., Barros, J.A.O. and Cunha, V.M.C.F. (2013) Relation between Fiber Distribution and Post-Cracking Behavior in Steel Fiber Reinforced Self-Compacting Concrete Panels. Cement and Concrete Research, 51, 57-66.

[5]   Marikunte, S., Aldea, C. and Shah, S.P. (1997) Durability of Glass Fiber Reinforced Cement Composites: Effect of Silica Fume and Metakaolin. Advanced Cement Based Materials, 5, 100-108.

[6]   Purnell, P., Short, N.R., Page, C.L., Majumdar, A.J. and Walton, P.L. (1999) Accelerated Aging Characteristics of Glass-Fiber Reinforced Cement made with New Cementitious Materials. Composites Part A: Applied Science and Manufacturing, 30, 1073-1080.

[7]   Enfedaque, A., Cendon, D., Galvez, F. and Sanchez-Galvez, V. (2010) Analysis of Glass Fiber Reinforced Cement (GRC) Fracture Surfaces. Construction and Building Materials, 24, 1302-1308.

[8]   Ozger, O.B., Girardi, F., Giannuzzi, G.M., Salomoni, V.A., Majorana, C.E., Fambri, L., Baldassino, N. and Di Maggio, R. (2013) Effect of Nylon Fibers on Mechanical and Thermal Properties of Hardened Concrete for Energy Storage Systems. Materials and Design, 51, 989-997.

[9]   Yap, S.P., Alengaram, U.J. and Jumaat, M.Z. (2013) Enhancement of Mechanical Properties in Polypropylene- and Nylon-Fiber Reinforced Oil Palm Shell Concrete. Materials and Design, 49, 1034-1041.

[10]   Song, P.S., Hwang, S. and Sheu, B.C. (2005) Strength Properties of Nylon- and Polypropylene-Fiber-Reinforced Concretes. Cement and Concrete Research, 35, 1546-1550.

[11]   Toutanji, H.A. (1999) Properties of Polypropylene Fiber Reinforced Silica Fume Expansive-Cement Concrete. Construction and Building Materials, 13, 171-177.

[12]   Stroeven, P. (2000) Development of Hybrid Polypropylene-Steel Fiber-Reinforced Concrete. Cement and Concrete Research, 30, 63-69.

[13]   Kurtz, S. and Balaguru, P. (2000) Postcrack Creep of Polymeric Fiber-Reinforced Concrete in Flexure. Cement and Concrete Research, 30, 183-190.

[14]   Tang, C.S., Shi, B., Gao, W., Chen, F.J. and Cai, Y. (2007) Strength and Mechanical Behavior of Short Polypropylene Fiber Reinforced and Cement Stabilized Clayey Soil. Geotextiles and Geomembranes, 25, 194-202.

[15]   Sukontasukkul, P. and Jamaswang, P. (2013) Use of Steel and Polypropylene Fibers to Improve Performance of Deep Soil-Cement Column. Construction and Building Materials, 29, 201-205.

[16]   Larson, B.K., Drzal, L.T. and Sorousian, P. (1990) Carbon Fiber-Cement Adhesion in Carbon Fiber Reinforced Cement Composites. Composites, 21, 205-215.

[17]   Toutanji, H.A., El-Korchi, T. and Katz, R.N. (1994) Strength and Reliability of Carbon-Fiber-Reinforced Cement Composites. Cement and Concrete Composites, 16, 15-21.

[18]   Graces, P., Fraile, J., Vilaplana-Ortego, E., Cazorla-Amoros, D., Alcocel, E.G. and Andion, L.G. (2005) Effect of Carbon Fibers on the Mechanical Properties and Corrosion Levels of Reinforced Portland Cement Mortars. Cement and Concrete Research, 35, 324-331.

[19]   Wang, C., Li, K.Z., Li, H.J., Jiao, G.S., Lu, J. and Hou, D.S. (2008) Effect of Carbon Fiber Dispersion on the Mechanical Properties of Carbon Fiber-Reinforced Cement-Based Composites. Materials Science and Engineering: A, 487, 52-57.

[20]   Yusof, N. and Ismail, A.F. (2012) Post Spinning and Pyrolysis Processes of Polyacrylonitirle (PAN)-Based Carbon Fiber and Activated Carbon Fiber: A Review. Journal of Analytical and Applied Pyrolysis, 93, 1-13.

[21]   Baeza, F.J., Galao, O., Zornoza, E. and Garces, P. (2013) Effect of Aspect Ratio on Strain Sensing Capacity of Carbon Fiber Reinforced Cement Composites. Materials and Design, 51, 1085-1094.

[22]   Sugama, T., Weber, L. and Brothers, L.E. (2002) Ceramic Fiber-Reinforced Calcium Aluminate/Flyash/Polyphosphate Cements at a Hydrothermal Temperature of 280°C. Advances in Cement Research, 14, 25-34.

[23]   Kakemi, M. and Hannant, D.J. (1996) Effect of Autoclaving on Cement Composites Containing Polypropylene, Glass and Carbon Fibres. Cement and Concrete Composites, 18, 61-66.

[24]   Sugama, T., Pyatina, T., Gill, S. and Kisslinger, K. (2012) Self-Decomposable Fibrous Bridging Additives for Temporary Cementitious Fracture Sealers in EGS Wells. BNL-101089-2012-IR, Brookhaven National Laboratory, Upton, NY.

[25]   Purnell, P., Short, N.R., Page, C.L. and Majumdar, A.J. (2000) Microstructural Observations in New Matrix Glass Fiber Reinforced Cement. Cement and Concrete Research, 30, 1747-1753.

[26]   Manget, P.S. and Gurusamy, K. (1987) Chloride Diffusion in Steel Fiber Reinforced Marine Concrete. Cement and Concrete Research, 17, 385-396.

[27]   Saremi, M. and Mahallati, E. (2002) A Study on Chloride-Induced Depassivation of Mild Steel in Simulated Concrete Pore Solution. Cement and Concrete Research, 32, 1915-1921.

[28]   Ghods, P., Isgor, O.B., McRae, G.A. and Gu, G.P. (2010) Electrochemical Investigation of Chloride-Induced Depassivation of Black Steel Rebar under Simulated Service Conditions. Corrosion Science, 52, 1649-1659.

[29]   Sugama, T., Kukacka, L.E., Carciello, N. and Galen, B. (1988) Oxidation of Carbon Fiber Surface for Improvement in Fiber-Cement Interfacial Bond at a Hydrothermal Temperature of 300°C. Cement and Concrete Research, 18, 290-300.

[30]   Sugama, T., Kukacka, L.E., Carciello, N. and Stathopoulos, D. (1989) Interfacial Reactions between Oxidized Carbon Fibers and Cements. Cement and Concrete Research, 19, 355-365.

[31]   Bao, Y., Ma, J. and Li, N. (2011) Synthesis and Swelling Behaviors of Sodium Carboxymethyl Cellulose-g-poly(AA-co-AM-co-AMPS)/MMT Superabsorbent Hydrogel. Carbohydrate Polymers, 84, 76-82.

[32]   Mishar, S., Rani, G.U. and Sen, G. (2012) Microwave Initiated Synthesis and Application of Polyacrylic Acid Grafted Carboxymethyl Cellulose. Carbohydrate Polymers, 87, 2255-2262.

[33]   Jing, M., Wang, C.g., Wang, Q., Bai, Y.J. and Zhu, B. (2007) Chemical Structure Evolution and Mechanism during Pre-Carbonization of PAN-Based Stabilized Fiber in the Temperature Range of 350 to 600°C. Polymer Degradation and Stability, 92, 1737-1742.

[34]   Ju, A.Q., Guang, S.Y. and Xu, H.Y. (2013) Effect of Comonomer Structure on the Stabilization and Spinnability of Polyacrylonitrile Copolymers. Carbon, 54, 323-335.