Portland Cement Mortar Composite with Partial Sand Replacement by Eggshell Particles
ABSTRACT
Agro-industrial activities generate a large amount of wastes. According to their specific properties, most of them can partially replace mineral aggregates, aiming to produce non-structural cement composites. In this research work, the behavior of a Portland cement mortar with partial replacement of sand by treated eggshell particles (0% to 66%) has been evaluated. Firstly, chemical compatibility between eggshell particles and Portland cement was carried by hydration curves. In a second step, a mixture of cement mortar based on treated eggshell (cold water, warm water and oven-dry) was prepared. Composite hardening was monitored by an ultrasound technique. At initial ages, ultrasonic pulse velocity (UPV) along the time was sensitivity enough to detect the sand-to-eggshell ratio effect. Compressive strength at 28 days ranged from 23 to 9 MPa depending on sand to eggshell particles ratio, which indicated that the composite was suitable for non-bearing structures, mainly at rural areas.

Cite this paper
Beraldo, A. (2014) Portland Cement Mortar Composite with Partial Sand Replacement by Eggshell Particles. Open Journal of Inorganic Non-metallic Materials, 4, 45-53. doi: 10.4236/ojinm.2014.44007.
References
[1]   Brazilian Institute of Geography and Statistics—IBGE.
http://www.ibge.gov.br

[2]   Freire, M.N. and Holanda, J.N.F. (2006) Characterization of Avian Eggshell Waste Aiming Its Use in a Ceramic Wall Tile Paste. Ceramica, 52, 240-244.
http://dx.doi.org/10.1590/S0366-69132006000400004

[3]   Shuhadah, S. and Supri, A.G. (2009) LDPE-Isophthalic Acid-Modified Egg Shell Powder Composites (LDPE/ESPI). Journal of Physical Science, 20, 87-98.

[4]   Da Silva, J.H.V. and Dos Santos, V.J. (2000) Calcium Carbonate Effect on the Eggshell Quality. Revista Brasileira de Zootecnia, 29, 1440-1445. (In Portuguese)

[5]   Amu, O.O. and Salami, B.A. (2010) Effect of Common Salt on Some Engineering Properties of Eggshell Stabilized Lateritic Soil. ARPN Journal of Engineering and Applied Sciences, 5, 64-73.

[6]   Hussein, A.A., Salim, R.D. and Sultan, A.A. (2011) Water Absorption and Mechanical Properties of High-Density Polyethylene/Egg Shell Composite. Journal of Basrah Researches (Sciences), 37, 36-42.

[7]   Huang, K.T., Liang, H.H. and Hung, M.J. (2010) Improvement in Fire Prevention Performance of Cork-Gypsum Decorative Materials by Applying Porous Waste. International Journal of the Physical Sciences, 5, 2038-2044.

[8]   Nagumo, C.H. and Beraldo, A.L. (2004) Eggshell and Portland Cement Mortar. Annals of ICTR—International Conference on Waste Treatment, Florianópolis, 2004, 2088-2097. (In Portuguese)

[9]   Nagumo, C.H. and Beraldo, A.L. (2005) Composite from Eggshell, Pinus Caribaea Waste and Portland Cement Mortar. Annals of XXIV CONBEA—Agricultural Engineering Congress, Canoas, 2005, 4 p. (In Portuguese)

[10]   Sandermann, W., Preusser, H.J. and Schiens, W. (1960) The Effect of Wood Extractives on the Setting of Cement-Bonded Wood Materials. Holzforschung, 14, 70-77.
http://dx.doi.org/10.1515/hfsg.1960.14.3.70

[11]   Weatherwax, R.C. and Tarkow, H. (1964) Effect of Wood on Setting of Portland Cement. Forest Products Journal, 14, 567-568.

[12]   Panzera, T.H., Christophoro, A.L., Cota, F.P., Borges, P.H.R. and Bowen, C.R. (2011) Chapter 17: Ultrasonic Pulse Velocity Evaluation of Cementitious Materials. In: Tesinova, P., Ed., Materials ScienceComposite Materials Advances in Composite Materials—Analysis of Natural and Man-Made Materials, Intech, Croácia, 411-436.
http://dx.doi.org/10.5772/17167

[13]   Beraldo, A.L. (1999) Ultrasonic Speed Wave: Cure Type Influence on Wood-Cement Composite Compression Strength. NDTISS’99—International Symposium on Nondestructive Testing Contribution to the Infrastructure Safety Systems in 21st Century, ABENDE-Brazilian Association of Non Destructive Testing, 1, 86-90.

[14]   Gül, R., Demirboga, R. and Güvercin, T. (2006) Compressive Strength and Ultrasound Pulse Velocity of Mineral Admixtured Mortar. Indian Journal of Engineering & Materials Sciences, 13, 18-24.

[15]   Brazilian Standard Technical Norms, ABNT (1991) NBR 5733. High Initial Strength Portland Cement. Specifications, Rio de Janeiro, 5 p. (In Portuguese)

[16]   Brazilian Standard Technical Norms, ABNT (1996) NBR 7215. Portland Cement: Compressive Strength Determination. Test Method, Rio de Janeiro, 8 p. (In Portuguese)

 
 
Top