Potentials of Bambusa vulgaris Grown in Southeast Nigeria for the Manufacture of Wood-Cement Composite Panels
ABSTRACT
In this work, the potentials of Bambusa vulgaris grown in southeast Nigeria for the manufacture of wood-cement composite panels were studied. Representative culms of Bambusa vulgaris were collected from a 4-year-old stand at lower Anambra river basin, southeast, Nigeria. Fiber morphological properties and proximate chemical analysis were determined in accordance with the provisions of the Technical Association of the Pulp and Paper Industries (TAPPI, 1998). Fiber slenderness ratio was 160.95:1, component solubility of 3.09, 5.60, and 19.8 percent for cold water soak for 24 hrs; hot water soak at 80°C for 1 hr, and 1% NaOH soak for 24 hrs respectively. Composite panels were made at 1200 kg/m3 and 800 kg/m3 density levels with flakes of different soak treatments (untreated/control; cold water soak for 24 hrs; water at 80°C soak for 1 hr and 1% NaOH soak for 24 hrs) at variable cement/B. vulgaris mix ratios (1:1, 1.5:1, 2:1, 2.5:1 and 3:1 wt/wt) with 3% CaCl2 as accelerator applied to the wood furnish before cement mixing. Prepared furnish was subjected to initial pre-pressing of 0.5 N/mm2 and final consolidation of 1.4 N/mm2 retained for 24 hrs. Panels were sampled and tested after 28 days for Modulus of Rupture (MOR) and Modulus of Elasticity (MOE) in bending and for water absorption (WA) and thickness swelling (TS) due to a 24-hr water soak. Test was in accordance with provisions of American Standard for Testing of Materials (ASTM-1998). Properties ranged from a low of 25.00 to 75.45 N/mm2 for MOR; 4128 to 15,065 N/mm2 for MOE; 15.01 to 36.11 percent for WA and 3.04 to 12.72 percent for TA. Effect of production mix on properties was determined using factorial analysis. Except for composite density whose effect was not significant at 0.05% level, all production mix was found significant at 0.01% level at the second order level of interactions. All panels met minimum property requirements of American National Standard Institute 208-2-1994 and 208-1-1993, British Standard (BS 5669, 1979) and Malaysian Standard (MS 934, 1984).

Cite this paper
Onuorah, E. , Nnabuife, E. and Nwabanne, J. (2014) Potentials of Bambusa vulgaris Grown in Southeast Nigeria for the Manufacture of Wood-Cement Composite Panels. Journal of Minerals and Materials Characterization and Engineering, 2, 363-373. doi: 10.4236/jmmce.2014.25041.
References
[1]   Kuriakose, S., Deviprasad, V. and Vaisakh, V.G. (2012) Mechanical Behaviour of Coir Reinforced Polyester Composite—An Experimental Investigation. International Journal of Emerging Technology and Advanced Engineering, 2, 751-757.

[2]   Fuwape, J.A. (2001) The Impacts of Forest Industries and Wood Utilization on the Environment. Journal of Tropical Forest Research, 17, 78-90.

[3]   Chen, X.H. (2000) The Sustainable Development of Wood Industry for the 21st Century. Forest Products and Industry, 26, 13.

[4]   Raw Materials Research and Development Council (RMRDC) (1996) Report on the Techno-Economic Survey of the Multi-Disciplinary Task Force on Pulp, Paper Products, Printing and Publishing Sector, Lagos, 33.

[5]   Lebel, P.W., Gunther, J., Webb, W., Clark, W.C., Food, B., Fasehun, F.E., Sanwo, S.K. and Bada, S.O. (1994) Review of Wood-Based Sector in Nigeia. Final Report Presented to FORMECU, Federal Ministry of Agric and Natural Resources, Abuja.

[6]   Agnihotri, S., Dutt, D. and Tyagi, C.H. (2010) Complete Characterization of Bagasse of Early Species of Saccharum officinerum—CO 89003 for Pulp and Paper Making. Bioresources, 5, 1197-1214.

[7]   Erakhrumen, A.A., Areghan, S.E., Ogunleye, M.B., Larinde, S.L. and Odeyale, O.O. (2008) Selected Physico-Mechanical Properties of Cement Bonded Particlboard Made from Pine (Pinus caribaea M.) Mixture. Scientific Research and Eassy, 3, 197-203.

[8]   Jorge, F.C., Pereira, C. and Ferreira, J.M.F. (2004) Wood-Cement Composites—A Review. Holz als Roh- und Werk- stoff, 62, 370-377. http://dx.doi.org/10.1007/s00107-004-0501-2

[9]   Youngquist, J.A. (1999) Wood-Based Composites and Panel Products. In: Wood Handbook: Wood as an Engineering Material. General Technical Report FPL-113, USDA, Forest Service, Forest Products Laboratory, Madison, Chapter 10, 1-31.

[10]   Jayabal, S., Sathiyamurthy, S., Loganathan, K.T. and Kalyanasundaram, S. (2012) Effect of Soaking Time and Concentration of NaOH Solution on Mechanical Properties of Coir-Polyester Composites. Bulletin of Materials Science, 3, 567-574. http://dx.doi.org/10.1007/s12034-012-0334-2

[11]   Bamisaye, J.A. (2007) Cement Bonded Particle Board Production from Rice Husk in Southern Nigeria. Journal of Engineering and Applied Sciences, 21, 183-185.

[12]   Chew, L.T., Sudin, R. and Kasim, J. (1992) Bambusa vulgaris for Urea and Cement-Bonded Particleboard Manufacture. Journal of Tropical Forest Science, 4, 249-256.

[13]   Badejo, S.O.O. (1987) An Investigation on the Influence of Cement Binder Content on Properties of Cement-Bonded Particle Board from Four Tropical Hardwoods. The Malaysian Forester, 50, 105-120.

[14]   Moslemi, A.A. and Pfister, S.C. (1987) The Influence of Cement-Wood Ratio and Cement Type on Bending Strength and Dimensional Stability of Wood-Cement Composite Panels. Wood and Fiber Science, 19, 165-175.

[15]   Onuorah, O.E. (2005) Properties of Fiberboards Made from Oil Palm (Elaeis guineensis) Stem and/or Mixed Tropical Hardwood Sawmill Residues. Journal of Tropical Forest Science, 17, 497-507.

[16]   (2009) Environmental Bamboo Foundation Why Bamboo.
www.bambooman.com.au/bambootreatment/ebf.php

[17]   Renuka, D.M., Poornima, N. and Guptan, P.S. (2007) Bamboo—The Natural, Green and Eco-Friendly New-Type Textile Material of the 21st Century. Journal of the Textile Association, 221-224.

[18]   Fangchun, Z. (1999) The 20th Century in Retrospect for Bamboo Trade and Prospects for the 21st Century. Journal of Bamboo Research, 4.

[19]   Claudio, H., Soares, D.M., Vinicius, G.C. and Mario, R.S. (2007) Production and Properties of Medium Density Wood-Cement Boards Produced with Oriented Strands and Silica Fume. Maderas Cienciay Technologia, 9, 105-115.

[20]   Ma, L.F. (2000) Manufacture of Bamboo-Cement Particleboard. Proceedings of the International Symposium on Trends of Wood Research and Utilization, Tokyo, 8.

[21]   Lee, A.W.C. and Short, P.H. (1989) Pretreating Hardwood for Cement-Bonded Excelsior Board. Forest Products Journal, 39, 68-70.

[22]   Keay, R.W.I., Onochie, C.F.A. and Standfield, D.O. (1964) Nigerian Trees. Vols. I & II. Federal Department of Forestry Research, Ibadan.

[23]   Liese, W. (1986) Anatomy and Properties of Bamboo. GTZ Publication, 196-207.

[24]   Technical Association of Pulp and Paper Industry (TAPPI) (1998) Test Methods. TAPPI Press, Atlanta, 1998.

[25]   Akpabio, U.D.I. (1989) The Effects of Mechanical Treatment and Blending of Tropical (Nigerian) Wood Pulps on Paper Properties. Nigerian Journal of Technical Education, 6, 32-43.

[26]   American Society for Testings and Materials (1998) Standard Test Methods for Evaluating Properties of Wood-Based Fiber and Particle Panel Materials. ASTM D1037-98, Annual Book of Standards, Philadephia.

[27]   Miller, I. and Freud, E.J. (1975) Probability and Statistics for Engineers. Prentice-Hall Inc., Englewood Cliffs.

[28]   Asasutjarit, C., Hirunlabh, J., Khedari, J., Daguenet, M. and Quenard, D. (2005) Coconut Coir Cement Board. International Conference on Durability of Building Materials and Components, Lyon, 17-20 April 2005.

[29]   Hunter, W.R. (2001) Nonwood Plant Fiber Characteristics. Hunter Consult Incorporated, Ottawa, 4.

[30]   Kelly, W.M. (1997) Critical Literature Review on Relationships between Processing Parameters and Physical Properties of Particleboard. General Technical FPL-10, USDA.

[31]   Ogunsile, B.O. and Uwajeh, C.F. (2009) Evaluation of the Pulp and Paper Potentials of a Nigerian Grown Bambusa vulgaris. World Applied Sciences Journal, 6, 536-541.

[32]   Olorunnisola, A.O. (2007) Effects of Particle Geometry and Chemical Accelerator on Strength Properties of Rattan-Cement Composite. African Journal of Science and Technology, 8, 22-27.

[33]   American National Standards Institute (1994) National Hardwood Association Standard for Medium Density Fiberboard (MFD). ANSI A 208-2-1994, Gaithersburg.

[34]   American National Standards Institute (1993) National Particle Board Association Standard for Particleboard. ANSI A 208-1-1993, Gaithersburg.

[35]   British Standard Institution (1979) Specifications for Wood Chipboard and Methods of Test for Particleboard. BS 5669:1979. British Standard Institution, London.

[36]   Malaysia Standard Institute—MS 934 (1984) Malaysian Standard Specification for Wood-Cement Board. SIRIM, Malaysia.

[37]   Oyagade, A.O. (2000) Thickness Swelling Components and Water Absorption of Cement-Bonded Particleboards Made from Gmelina Wood, Bagasse and Coconut Husk. Nigerian Journal of Forestry, 30, 10-14.

 
 
Top