Effect of Shakeout Time on Microstructure and Hardness Properties of Grey Cast Iron
ABSTRACT
Solidification process of grey cast iron largely determines the resultant carbon precipitates in form of graphite or carbides. Microstructure and hardness properties of grey iron were therefore studied. Aggregate scraps were melted with varying inoculants composition of 0.1 wt%, 0.2 wt% and 0.3 wt%. Cast produced was shaken out of the mould at various timing. Microstructures of the samples were determined and analyzed. Hardness properties were equally evaluated. It was observed that the occurrence of carbides was more with 0.25 hrs shakeout time than other varying timing. Increasing shakeout time was found to decrease hardness and increase the carbide grain size. When the ferrosilicon content increases, there is a gradual decrease in the hardness properties from 59.6 HRC to 53.2 HRC for 0.25 hrs shakeout time cast sample. Similar decreases were observed for various timing analyzed.

Cite this paper
Seidu, S. , Oloruntoba, D. and Otunniyi, I. (2014) Effect of Shakeout Time on Microstructure and Hardness Properties of Grey Cast Iron. Journal of Minerals and Materials Characterization and Engineering, 2, 346-350. doi: 10.4236/jmmce.2014.24039.
References
[1]   Kurz, W. and Fisher, D.J. (1986) Solidification of Single-Phase Alloys, Principle of Solidification. Trans Tech Publications Ltd., 121.

[2]   Beno, J. and Jelinek, P. (2009) Solution of Negative Impact of Carbonaceous Additive to Bentonite Mixtures. International PhD Foundry Conference.

[3]   Tonkovic, M.P., Jovoz, V. and Igorz, M. (2009) The Effect of Inoculants on Hardness and Machinability of Grey Cast Iron with Flake Graphite. Materials and Geoenvironment, 58, 521-530.

[4]   Elkem, A.S. (2009) Cast Iron Inoculation—The Technology of Graphite Shape Control. Foundry Products Division, Oslo.

[5]   Ojo, S.O. and Riposan, I. (2012) Alloy Selection for in Mould Inoculation to Control Chill Width in Ductile Iron Institute of Materials, Minerals and Mining. Material Science and Technology, 28, 576-581. http://dx.doi.org/10.1179/1743284711Y.0000000117

[6]   Seidu, S.O. and Ogunniyi, I.O. (2013) Control of Chilling Tendency in Grey Cast Iron Reuse. Materials Research, 16, 145-149. http://dx.doi.org/10.1590/S1516-14392012005000160

[7]   Jain, P.L. (1997) Principles of Foundry Technology. Tata McGraw-Hill, India.

[8]   Flin, R. (1963) Fundamentals of Metal Casting. Addison-Lee, New York.

[9]   Kehl, G.L. (1949) The Principles of Metallographic Laboratory Practice.

[10]   Hughes, K.V. (1994) Practical Microscopical Metallography. University of Missouri Extension, Columbia Publication.

[11]   Krause, D.E. (1969) Grey Iron—A Unique Engineering Material. ASTM Special Technical Publication, Philadelphia, 3-28.

 
 
Top