Calcined Clay Pozzolan as an Admixture to Mitigate the Alkali-Silica Reaction in Concrete
ABSTRACT


Calcined clay pozzolan has been used to replace varying portions of high alkali Portland limestone cement in order to study its effect on the alkali-silica reaction (ASR). Portland limestone cement used for the study had a total Na2Oeq of 4.32. Mortar-bar expansion decreased as pozzolan content in the cement increased. The highest expansion was recorded for reference bars with no pozzolan, reaching a maximum of 0.35% at 42 days whilst the expansion was reduced by between 42.5% and 107.8% at 14 days and between 9.4% and 16.4% at 84 days with increasing calcined clay pozzolan content. Mortar bars with 25% pozzolan were the least expansive recording expansion less than 0.1% at all test ages. X-ray diffractometry of the hydrated blended cement paste powders showed the formation of stable calcium silicates in increasing quantities whilst the presence of expansive alkali-silica gel, responsible for ASR expansion, decreased as pozzolan content increased. The study confirms that calcined clay pozzolan has an influence on ASR in mortar bars and causes a significant reduction in expansion at a replacement level of 25%.



Cite this paper
Sarfo-Ansah, J. , Atiemo, E. , Boakye, K. , Adjei, D. and Adjaottor, A. (2014) Calcined Clay Pozzolan as an Admixture to Mitigate the Alkali-Silica Reaction in Concrete. Journal of Materials Science and Chemical Engineering, 2, 20-26. doi: 10.4236/msce.2014.25004.
References
[1]   American Society for Testing and Materials (2000) 2000 Annual Book of ASTM Standards: Part 14-C 150. Specification for ordinary Portland cement, ASTM, Philadelphia, 101-107.

[2]   Multon, S., Sellier, A. and Cyr, M. (2009) Chemo-Mechanical Modeling for Prediction Of Alkali-Silica Reaction (ASR) Expansion. Cement and Concrete Research, 39, 490-500.

[3]   Taylor, H.F.W. (1997) Cement Chemistry. 2nd Edition, Thomas Telford Publishing, London, 361.
http://dx.doi.org/10.1680/cc.25929

[4]   Sims, I. and Brown, B. (1998) Concrete Aggregates: Chapter 16 in Lea’s Chemistry of Cement and Concrete. 4th Edition, Elsevier, Oxford, 963.

[5]   Tong, L. and Tang, M. (1999) Expansion Mechanism of Alkali-Dolomite and Alkali-Magnesite Reaction. Cement and Concrete Research, 21, 361-373.
http://dx.doi.org/10.1016/S0958-9465(99)00022-0

[6]   Malvar, L.J., Cline, G.D., Burke, D.F., Rollings, R., Sherman, T.W. and Greene, J. (2002) Alkali-Silica Reaction Mitigation: State-Of-The-Art and Recommendations. ACI Materials Journal, 99, 1-25.

[7]   American Society for Testing and Materials (2000) 2000 Annual Book of ASTM Standards: Part 14-C 289. Standard Test Method for Potential Reactivity of Aggregates (Chemical Method), ASTM, Philadelphia, 187-195.

[8]   American Society for Testing and Materials (2007) ASTM C 1260-07; Standard Test Method for Potential Reactivity of Aggregates (Mortar-Bar Method)1, ASTM, Philadelphia, 1-5.

[9]   American Society for Testing and Materials (2008) ASTM C 1293-08; Standard Test Method for Determination of Length Change of Concrete Due to Alkali-Silica Reaction. ASTM, Philadelphia.

[10]   Kandasamy, S. and Shehata, M.H (2014) Thecapacity of Ternary Blends Blends Containing Slag and High-Calcium Fly Ash to Mitigate Alkali Silica Reaction. Cement and Concrete Research, 49, 92-99.
http://dx.doi.org/10.1016/j.cemconcomp.2013.12.008

[11]   Canadian Standards Association (2009) CAN/CSA-A23.2-14A-09: Potential Expansivity of Aggregates; Procedure for Length Change Due to Alkali-Aggregate Reaction in Concrete Prisms. CSA, Ontario.

[12]   Aquino, W., Lange, D.A. and Olek, J. (2001) The Influence of Metakaolin and Silica Fume on the Chemistry of Alkali-Silica Reaction Products. Cement and Concrete Research, 23, 485-493.
http://dx.doi.org/10.1016/S0958-9465(00)00096-2

[13]   Ramlochan, T., Thomas, M. and Gruber, K.A. (2000) The Effect of Metakaolin on Alkali-Silica Reaction in Concrete. Cement and Concrete Research, 30, 339-344.
http://dx.doi.org/10.1016/S0008-8846(99)00261-6

[14]   Turanli, L., Bektas, F. and Monteiro, P.J.M. (2003) Use of Ground Clay Brick as a Pozzolanic Material to Reduce the Alkali-Silica Reaction. Cement and Concrete Research, 33, 1539-1542.
http://dx.doi.org/10.1016/S0008-8846(03)00101-7

[15]   Karakurt, C. and Topçu, I.B. (2011) Effect of Blended Cements Produced with Natural Zeolite and Industrial By-Products on Alkali-Silica Reaction and Sulfate Resistance of Concrete. Construction and Building Materials, 25, 1789-1795.
http://dx.doi.org/10.1016/j.conbuildmat.2010.11.087

[16]   Walters, G.V. and Jones, T.R. (1991) Effect of Metakaolin on Alkali-Silica Reaction (ASR) in Concrete Manufactured with Reactive Aggregate. ACI Special Publication, 126, 941-954.

[17]   Kostuch, J.A., Walters, G.V. and Jones, T.R (2003) High Performance Concrete Incorporating Metakaolin—A Review. Proceedings of the International Conference on Advances in Concrete and Structures: Concrete 2000, 17-19 September 2003, Xuzhou, 1799-1811.

[18]   European Committee for Standardization (2000) European Standard EN 197-1, Composition, Specifications and Conformity Criteria for Common Cements. European Committee for Standardization, Brussels, 15.

[19]   European Committee for Standardization (2002) European Standard EN 12620, Aggregates for Concrete. European Committee for Standardization, Brussels, 28.

[20]   American Society for Testing and Materials (2000) 2000 Annual Book of ASTM Standards: Part 14-C33; Specification for Concrete Aggregate. ASTM, Philadelphia, 16.

[21]   Wang, A.Q., Zhang, C.Z., Tang, M.S. and Zhang, N.S. (1999) ASR in Mortar Bars Containing Silica Glass in Combination with High Alkali and High Fly Ash Contents. Cement and Concrete Composites, 21, 375-381.
http://dx.doi.org/10.1016/S0958-9465(99)00020-7

[22]   Topçu, I.B., Boga, A.R. and Bilir, T (2008) Alkali-Silica Reactions of Mortars Produced by Using Waste Glass as Fine Aggregate and Admixtures such as Fly Ash and Li2CO3. Waste Management, 28, 878-884.
http://dx.doi.org/10.1016/j.wasman.2007.04.005

[23]   BSI (1990) British Standards 1377 (Part 2): Methods of Test for Soils for Civil Engineering Purposes—Classification Tests. BSI, London, 42.

[24]   American Society for Testing and Materials (2000) 2000 Annual Book of ASTM Standards: Part 13-C 204; Standard Test Method for Fineness of Portland Cement by Air Permeability Method. ASTM, Philadelphia, 195-201.

[25]   American Society for Testing and Materials (2000) 2000 Annual Book of ASTM Standards: Part 14-C 490; Standard Specification for Apparatus for Use in Measurement of Length Change of Hardened Cement Paste, Mortar and Concrete. ASTM, Philadelphia.

[26]   American Society for Testing and Materials (2000) 2000 Annual Book of ASTM Standards: Part 14-C 618; Standard Specification for Fly Ash and Raw or Calcined Natural Pozzolana for Use as a Mineral Admixture in Portland Cement Concrete. ASTM, Philadelphia, 355-358.

[27]   Ichikawa, T. (2009) Alkali-Silica Reaction, Pessimum Effects and Pozzolanic Effect. Cement and Concrete Research, 39, 716-726.
http://dx.doi.org/10.1016/j.cemconres.2009.06.004

 
 
Top