JBM  Vol.2 No.2 , April 2014
In Vivo Evaluation of Titanium Implants Bioactivated by a Modified Kokubo’s Treatment
Abstract: In this study a modified Kokubo’s treatment (MKT) was used to bioactivate titanium implants. Titanium surfaces were alumina-blasted and etched in HCl/H2SO4 solution followed by treatment in autoclave at 120°C for 1, 3, 5 hour periods with chemical solutions containing 1, 2 and 3 M of NaOH. The materials were characterized by surface angle measurements, roughness, field emission scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS), and in vivo tests. Statistical analysis by polynomial regression showed that solutions within 2.2 and 2.8 M NaOH lead to surface contact angles close to zero degree after 1 h of treatment. XPS analysis carried out on a sample treated 1 h in 2.2 M NaOH indicated the presence of a titanate film. This solution was selected to treat titanium implants for in vivo tests. These tests were performed on sheep in three types of separating surfaces: machined group (standard), SLA group (A) and MKT group (B) divided into two time intervals of 3 and 6 weeks. The samples in group B displayed better results compared to group A only after 6 weeks in terms of counter torque and bone implant contact (BIC).
Cite this paper: Jesus, J. , Gemelli, E. , Nery, F. and Camargo, N. (2014) In Vivo Evaluation of Titanium Implants Bioactivated by a Modified Kokubo’s Treatment. Journal of Biosciences and Medicines, 2, 22-29. doi: 10.4236/jbm.2014.22004.

[1]   Liu, X., Chu, P.K. and Ding, C. (2010) Surface Nano-Functionalization of Biomaterials. Materials Science and Engineering R, 70, 275-302.

[2]   Branemark, P.I., Hansson, B.O., Adell, R., Breine, U., Lindström, U., Hallén, O. and Oman, A. (1977) Osseointegrated Implants in the Treatment of the Edentulous Jaw. Experience from a 10-Year Period. Scandinavian Journal of Plastic and Reconstructive Surgery, 16, 7-127.

[3]   Albrektsson, T. and Wennerberg, A. (2004) Oral Implant Surfaces: Part 1-Review Focusing on Topo-graphic and Chemical Properties of Different Surfaces and in Vivo Responses to Them. International Journal of Pros-thodontics, 17, 536-543.

[4]   Albrektsson, T., Branemark, P.I., Hansson, H.A. and Lindström, J. (1981) Osseointe-grated Titanium Implants. Acta Orthopaedica Scandinavica, 52, 155-179.

[5]   Novaes Jr., A.B., Souza, S.L.S., Barros, R.R.M., Pereira, K.K.Y., Iezzi, G. and PiattellI, A. (2010) Influence of Implant Surfaces on Osseointegration. Brazilian Dental Journal, 21, 471-481.

[6]   Junker, R., Dimakis, A., Thoneick, M. and Jansen, J.A. (2009) Effects of Implant Surface Coatings and Composition on Bone Integration: A Systematic Review. Clinical Oral Implants Research, 20,185-206.

[7]   Buser, D., Broggini, N., Wieland, M., Schenk, R.K., Denzer, A.J., Cochran, D.L., Hoffmann, B., Lussi, A. and Steinemann, S.G. (2004) Enhanced Bone Apposition to a Chemically Modified SLA Titanium Surface. Journal of Dental Research, 83, 529-533.

[8]   Zhao, G., Schwartz, Z., Wieland, M., Rupp, F., Geis-Gerstorfer, J., Cochran, D.L. and Boyan, B.D. (2005) High Surface Energy Enhances Cell Response to Titanium Substrate Micro-structure. Journal of Biomedical Materials Research Part A, 74, 49-58.

[9]   Rihova, Z., Stary, V. and Bacakova, L. (2012) A Study of the Structure and Surface Properties of Nanostructured Biocompatible Coatings on Ti Alloys. Vacuum, 86, 630-633.

[10]   Lu, X., Zhao, Z. and Leng, Y. (2007) Biomimetic Calcium Phosphate Coatings on Nitric-Acid-Treated Titanium Surfaces. Materials Science and Engineering C, 27, 700-708.

[11]   Kilpadi, D.V. and Lemons, J. E. (1994) Surface Energy Characterization of Unalloyed Titanium Implants. Journal of Biomedical Materials Research, 28, 1419-1425.

[12]   Rupp, F., Scheideler, L., Olshanska, N., de Wld, M., Wieland, M. and Geis-Gesttorfer, J. (2006) Enhancing Surface Free Energy and Hydrophilicity through Modification of Microstructured Titanium Implant Surface. Journal of Biomedical Materials Research, 76, 323.

[13]   An, S.-H., Matsumoto, T., Miyajima, H., Sasaki, J.-I., Narayanan, R. and Kim, K.-H. (2012) Surface Characterization of Alkali- and Heat-Treated Ti with or without Prior Acid Etching. Applied Surface Science, 258, 4377-4382.

[14]   Kim, H. M., Miyaji, F., Kokubo, T. and Nakamura, T. (1996) Preparation of Bioactive Ti and Its Alloys via Simple Chemical Surface Treatment. Journal of Biomedical Materials Research, 32, 409-417.<409::AID-JBM14>3.0.CO;2-B

[15]   Park, J.H., Wasilewski, C.E., Almodovar, N., Olivares-Navarrete, R., Boyan, B.D., Tannenbaum, R. and Schwartz, Z. (2012) The Responses to Surface Wettability Gradients Induced by Chitosan Nanofilms on Microtextured Titanium Mediated by Specific Integrin Receptors. Biomaterials, 33, 7386-7393.

[16]   Bornstein, M.M., Wittneben, J.G., Bragger, U. and Buser, D. (2010) Early Loading at 21 Days of Non-Submerged Titanium Implants with a Chemically Modified Sandblasted and Acid-Etched Surface. 3-Year Results of a Prospective Study in the Posterior Mandible. Journal of Periodontology, 81, 809-818.

[17]   Kokubo, T. and Yamaguchi, S. (2010) Novel Bioactive Ti-tanate Layers Formed on Ti Metal and Its Alloys by Chemical Treatments. Materials, 3, 48-63.

[18]   Davies, J.E. (2003) Understanding Peri-Implant Endosseous Healing. Journal of Dental Education, 67, 932-949.

[19]   Kokubo, T., Matsushita, T. and Takadama, H. (2007) Titania-Based Bioactive Materials. Journal of the European Ceramic Society, 27, 1553-1558.

[20]   Chen, Y., Zheng, X., Ji, H. and Ding, C. (2007) Effect of Ti-OH Formation on Bioactivity of Vacuum Plasma-Sprayed Titanium Coating after Chemical Treatment. Surface and Coatings Technology, 202, 494-498.