Effect of Toluene and Dioctylphthalate on the Rebar Corrosion of Medium Carbon Steel in Seawater and Cassava Fluid
ABSTRACT
Chemical mitigation is regularly used as one of the principal prevention and control techniques in reinforcement corrosion. Hence this study presents the effect of toluene and dioctylphthalate on the rebar corrosion of medium carbon steel in seawater and cassava fluid with a view to determining inhibitive potentials of the different inhibitors in the two media. Gravimetric and voltametric techniques were employed in this study and a total of forty-five corrosion coupons of different dimensions were produced. Forty coupons were used for gravimetry and the remaining five for corrosion potentials measurements. Eight of the samples were used as control; while other eight samples were admixed with dioctylphthalate and toluene in concrete cubes. It was later immersed in seawater and cassava fluid for a total duration of 32 days and the measurements were taken at interval of 4 days in order to determine the corrosion rates in mils per year (mmpy). Two controls and admixed samples were later immersed in seawater and cassava fluid, respectively, for durations of thirty-two days to determine the corrosion potentials using a voltmeter and a Copper-Copper Sulphate Electrode (Cu/CuSO4). The pH of each medium was also measured throughout the period of exposure. The results obtained showed that all the samples except the control samples, displayed some degree of inhibition. The inhibition levels for the admixed samples in seawater were on the higher side compared with those in cassava fluid. The inhibition efficiencies for different inhibitors followed different trends in different environment. The inhibition efficiencies for toluene in cassava fluid and seawater were 21.64% and 45.78% respectively. The study concluded that organic inhibitors were effective in inhibiting corrosion in cyanide and chloride contaminated concrete cubes.

Cite this paper
Adamu, M. , Umoru, L. and Ige, O. (2014) Effect of Toluene and Dioctylphthalate on the Rebar Corrosion of Medium Carbon Steel in Seawater and Cassava Fluid. Journal of Minerals and Materials Characterization and Engineering, 2, 1-7. doi: 10.4236/jmmce.2014.21001.
References
[1]   M.G. Fontana, “Corrosion Engineering,” 3rd Edition, B & Jo Enterprise Pte Ltd., Singapore, 1988, p. 443.

[2]   H. A. Ali, “The Effect of a Waste-Products Mix on Concrete Strength and Protection of Steel Reinforcement in Sulphate Media,” Journal of Corrosion Prevention and Control, Vol. 46, No. 3, 1999, p. 76.

[3]   M. M. Nasar, “The Effect of Environmental Temperature on the Corrosion of Reinforced Concrete,” Journal of Corrosion Prevention and Control, Vol. 44, No. 9, 1997, pp. 167-172.

[4]   R. D. Browne, “Mechanisms of Corrosion of Steel in Concrete in Relation to Design, Inspection, Repair of Offshore and Coastal Structures, Performances of Concrete in Marine Environment,” American Concrete Institute, Farmington Hills, Sp-65, 1980, p. 169.

[5]   V. A. Oyenuga and E. O. Amazigo, “A Note on Hydrocyanic Content of Cassava,” West African Journal of Biological Chemistry, Vol. 1, No. 2, 1957, pp. 29-43.

[6]   W. H. Ailor, “Handbook on Corrosion Testing and Evaluation,” Wiley, Etobicoke, 1964, pp. 1150-1165.

[7]   F. G. Fontana and N. D. Greene, “Corrosion Engineering,” McGraw-Hill, New York, 1978, p. 59.

[8]   E. H. Norman, “NACE Glossary of Corrosion Terms,” Materials Protection, Vol. 4, No. 1, 1965, p. 79.

[9]   C. C. Nathan, “Corrosion Inhibitors,” National Association of Corrosion Engineers (NACE), Houston, 1973, p. 279.

[10]   S. W. Dean Jr., “Inhibitor Type,” Material Performance, Vol. 20, No. 11, 1981, pp. 47-51.

[11]   V. S. Ramachandran, “Concrete Admixtures Handbook: Properties, Science and Technology,” 5th Edition, Noyes Publications, Park Ridge, New Jersey, 1984, p. 626.

[12]   H. Konno, S. K. Obayashi, H. Takahash and M. Nagayama, “The Hydration of Barrier Oxide Films on ions,” Corrosion Science, Vol. 10, pp. 913-923.

[13]   H. S. Isaacs, S. Virtanen, M. P. Ryan, P. Schmuki and L. J. Oblonsky, “Incorporation of Cr in the Passive Film on Fe from Chromate Solutions,” Electrochimica Acta, Vol. 47, No. 19, 2002, pp. 3127-3130.
http://dx.doi.org/10.1016/S0013-4686(02)00231-1

[14]   P. Montes, T. W. Bremner and D. H. Lister, “Influence of Calcium Nitrite Inhibitor and Crack Width on Corrosion of Steel in High Performance Concrete Subjected to a Simulated Marine Environment,” Cement and Concrete Composites, Vol. 26, No. 3, 2004, pp. 243-253.
http://dx.doi.org/10.1016/S0958-9465(03)00043-X

[15]   K. K. Sideris and A. E. Savva, “Durability of Mixtures Containing Calcium Nitrite Based Corrosion Inhibitor,” Cement & Concrete Composites, Vol. 27, No. 2, 2005, pp. 277-287.
http://dx.doi.org/10.1016/j.cemconcomp.2004.02.016

[16]   N. Hackerrman, “Fundamentals of Inhibitors,” NACE Basic Corrosion Course, NACE, Houston, 1965.

[17]   S. Craig, “Welding Technology Today Principles and Practices,” Prentice-Hall, Inc., Upper Saddle River, 1989, p. 301.

[18]   D. F. H. Rasheeduzzafar and A. S. Al-Gahtani, “Corrosion of Reinforcement in Concrete Structures in the Middle East,” Concrete International: Design and Construction, Vol. 7, No. 9, 1985, pp. 48-55.

[19]   O. S. B. Al-Amoudi and M. Maslehuddin, “The Effect of Chloride and Sulphate ions on Reinforcement Corrosion,” Cement and Concrete Research, Vol. 23, No. 1, 1993, pp. 139-146.
http://dx.doi.org/10.1016/0008-8846(93)90144-X

[20]   O. S. B. Al-Amoudi, S. N. Abduljauwad, A. Rasheeduzzafar and M. Maslehuddin, “Effect of Chloride and Sulphate Contamination in Soils on Corrosion of Steel and Concrete,” Transportation Research Record No. 1345, Transportation Research Board, Washington DC, 1992, pp. 67-73.

[21]   S. Popovics, “Strength and Related Properties of Concrete: A Quantitative Approach,” John Wiley & Sons, Inc., New York, 1998, p. 122.

[22]   M. Maslehuddin and O. S. B. Al-Amoudi, “Corrosion of Reinforcing Steel in Concrete: Its Monitoring and Preventions,” Symposium on Corrosion and Its Control, Preprint, King Saud University, Riyadh, 1992, pp. 80-90.

[23]   M. G. Fontana and N. D. Greene, “Corrosion Engineering,” McGraw-Hill Book Co., New York, 1996, pp. 28-116.

[24]   A. A. Akindahunsi, G. Oboh and A. A. Oshodi, “Effect of Fermenting Cassava with Rhizopus Oryzae on the Chemical Composition of Its Flour and Garri,” Rivista Italiana delle Sostanze Grasse, Vol. 7, No. 6, 1999, pp. 437-440.

[25]   M. G. Fontana and N. D. Greene, “Corrosion Engineering,” McGraw-Hill, New York, 1978, p. 59.

[26]   O. E. Olorunniwo, L. E. Umoru and O. R. Bamigboye, “Sodium Chromate and Diethylene Amine as Corrosion Inhibitors for Mild Steel in Cassava Fluid,” Journal of Applied Science, Vol. 4, No. 6, 2008, pp. 878-882.

[27]   R. E. West and W. G. Hime, “Chloride Profiles in Salty Concrete,” Materials Performance, Vol. 5, 1975, pp. 29- 36.

[28]   A. O. James and O. Akaranta, “The Inhibition of Corrosion of Zinc in 2.0 M Hydrochloric Acid Solution with Acetone Extract of Red Onion Skin,” African Journal of Pure and Applied Chemistry, Vol. 3, No. 11, 2009, pp. 212-217.

[29]   J. Cruz, R. Martinez, J. Genesca and E. Garcia-Ochoa, “Experimental and Theoretical Study of 1-(2-ethylamino)-2 Methylimidazoline as an Inhibitor of Carbon Steel Corrosion in Acid Media,” Journal of Electroanalytical Chemistry, Vol. 566, No. 1, 2004, pp. 111-121.
http://dx.doi.org/10.1016/j.jelechem.2003.11.018

[30]   N. Hackerman and E. S. Snavely, “Corrosion Basics: An Introduction,” NACE, Houston, TX, 1984, pp. 127-146.

 
 
Top