Hot Corrosion Behavior of Sol-Gel Nano Structured Zirconia Coated 9Cr1Mo Ferritic Steel in Alkali Metal Chlorides and Sulphates Deposit Systems at High Temperatures
ABSTRACT

Fused salt accelerated hot corrosion is quite common in gas turbines, fossil fuelled devices, waste inclinators, pyrochemical systems, etc. Presence of fused salt on metal surface dissolves their existing oxide layer. This results in an increase in oxidation rate of the metal. Since, zirconia coating is well recognized for corrosion protection under high temperature oxidative environment, we have developed zirconia coating on 9Cr1Mo ferritic steel and their oxidation performance was evaluated in LiCl-NaCl and Na2SO4-K2SO4 salts deposit system in air atmosphere at 650?C and 850?C, respectively. Before coating development, zirconium based sol was synthesized using zirconium (IV) propoxide as a precursor. Oxidation test results indicated that the zirconia coated specimens shows more than two times higher corrosion resistance in LiCl-NaCl and three time higher corrosion resistance in Na2SO4-K2SO4 salt deposit, respectively.


Cite this paper
G. Ruhi, O. Modi and I. Singh, "Hot Corrosion Behavior of Sol-Gel Nano Structured Zirconia Coated 9Cr1Mo Ferritic Steel in Alkali Metal Chlorides and Sulphates Deposit Systems at High Temperatures," Journal of Surface Engineered Materials and Advanced Technology, Vol. 3 No. 1, 2013, pp. 55-60. doi: 10.4236/jsemat.2013.31A008.
References
[1]   J. Stringer, “High Temperature Corrosion of Aerospace Alloys,” AGARD AG, 1975, p. 200.

[2]   J. Stringer, “Hot Corrosion of High Temperature Alloys,” Materials Research, Vol. 7, 1977, pp. 477 509. doi:10.1146/annurev.ms.07.080177.002401

[3]   Y. H. Sohn, R. R. Biederman and R. D. Sisson, “Micro structural Development in Physical Vapour Deposited Partially Stabilized Zirconia Thermal Barrier Coatings,” Thin Solid Films, Vol. 250, No. 1 2, 1994, p. 201. doi:10.1016/0040 6090(94)90155 4

[4]   G. M. Ingo, “Origin of Darkening in 8 wt% Yttria—Zir conia Plasma Sprayed Thermal Barrier Coatings,” Jour nal of the American Ceramic Society, Vol. 74, No. 2, 1991, pp. 381 386. doi:10.1111/j.1151 2916.1991.tb06891.x

[5]   A. Nazeri and S. B. Qadri, “Alumina Stabilized Zirconia Coatings for High Temperature Protection of Turbine Blades,” Surface and Coatings Technology, Vol. 86 87, Pt. 1, 1996, pp. 166 169. doi:10.1016/S0257 8972(96)03025 3

[6]   Y. S. Baron, A. Ruiz and G. Navas, “High Temperature Oxidation Resistance of 1.25cr 0.5 mo wt% Steels by Zirconia Coating,” Surface and Coatings Technology, Vol. 202, No. 12, 2008, pp. 2616 2622. doi:10.1016/j.surfcoat.2007.09.038

[7]   H. Li, K. Liang, L. Mei, S. Gu and S. Wang, “Oxidation Protection of Mild Steel by Zirconia Sol Gel Coatings,” Materials Letters, Vol. 51, No. 4, 2001, pp. 320 324. doi:10.1016/S0167 577X(01)00311 1

[8]   C. Sanchez, J. Livage, M. Henry and F. Babonneau, “Chemical Modification of Alkoxide Precursors,” Journal of Non Crystalline Solids, Vol. 100, No. 1 3, 1988, pp. 65 76. doi:10.1016/0022 3093(88)90007 5

[9]   M. Guglielmi and G. Carturan, “Precursors for Sol Gel Preparations,” Journal of Non Crystalline Solids, Vol. 100, No. 1 3, 1988, pp. 16 30. doi:10.1016/0022 3093(88)90004 X

[10]   K. Lzumi, M. Murakami, T. Deguchi and A. Morita, “Zir conia Coating on Stainless Steel Sheets from Organozir conium Compounds,” Journal of the American Ceramic Society, Vol. 72, No. 8, 1989, pp. 1465 1468. doi:10.1111/j.1151 2916.1989.tb07677.x

[11]   S. Hirai, K. Shimakage and S. Aizawa, “Alkaline Corro sion Resistance of Anodized Aluminum Coated with Zir conium Oxide by a Sol Gel Process,” Journal of the American Ceramic Society, Vol. 81, No. 12, 1998, pp. 3087 3092. doi:10.1111/j.1151 2916.1998.tb02742.x

[12]   R. Dimaggio, L. Fedrizzi, S. Rossi and P. Scardi, “Dry and Wet Corrosion Behaviour of AISI 304 Stainless Steel Coated by Sol Gel ZrO2 CeO2 Films,” Thin Solid Films, Vol. 286, No. 1 2, 1996, pp. 127 135. doi:10.1016/S0040 6090(95)08515 7

[13]   M. Atik, C. P. Kha, P. Delimaneto, L. A. Avaca, M. A. Aegerter and J. Zarzycki, “Protection of 316L Stainless Steel by Zirconia Sol Gel Coatings in 15% H2SO4 Solu tions,” Journal of Materials Science Letters, Vol. 14, No. 3, 1995, pp. 178 181. doi:10.1007/BF00318248

[14]   M. Shane and M. L. Mecartney, “Sol Gel Synthesis of Zirconia Barrier Coatings,” Journal of Materials Science, Vol. 25, No. 3, 1990, pp. 1537 1544. doi:10.1007/BF01045347

[15]   G. Ehrhart, B. Capoen, O. Robbe, Ph. Boy, S. Turrell and M. Bouazaoui, “Structural and Optical Properties of n Propoxide Sol Gel Derived ZrO2 Thin Films,” Thin Solis Films, Vol. 496, No. 2, 2006, pp. 227 233. doi:10.1016/j.tsf.2005.08.309

[16]   K. W. Tenze, K. Valle, L. Bianchi, P. Belleville and N. Caron, “Nanostructured Zirconia Coatings Processed by PROSOL Deposition,” Surface and Coatings Technology, Vol. 202, No. 18, 2008, pp. 4349 4354. doi:10.1016/j.surfcoat.2008.04.008

[17]   K. H. Yoon, Y. S. Cho and D. H. Kang, “Molten Salt Synthesis of Lead Based Relaxors,” Journal of Materials Science, Vol. 33, No. 12, 1998, pp. 2977 2984. doi:10.1023/A:1004310931643

[18]   J. Stringer, High Temperature Technologies, Vol. 3, 1985, p. 119.

[19]   D. C. Bradley, R. C. Mehrotra and D. P. Gaur, “Metal Alkoxides,” Academic Press, New York, 1978, p. 27.

[20]   U. B. Saxena, A. K. Rai, V. K. Mathur and R. C. Mehrotra, Journal of the Chemical Society, Vol. A, 1970, p. 904.

[21]   R. Brenter and A. Gagnaire, “Densification and Aging of ZrO2 Films Prepared by Sol Gel,” Thin Solid Films, Vol. 392, No. 1, 2001, pp. 142 148. doi:10.1016/S0040 6090(01)01009 4

[22]   Q. F. Quinson, G. Chino, M. D. Becdelievre, L. Guizar and H. Brunel, Journal of Materials Science, Vol. 31, 1996, p. 5.

[23]   R. A. Rapp and K. S. Goto, 2nd International Symposium, Molten Salts, J. Braunstein, Ed., The Electrochemical Society, New Jersey, 1981, p. 81.

 
 
Top