The Reaction Sequence and Dielectric Properties of BaAl2Ti5O14 Ceramics
ABSTRACT
To investigate the correct reaction sequence of BaO-Al2O3-5TiO2 system, powders calcined at different temperatures are analyzed by x-ray diffraction. The results show that the source phase BaCO3 decomposes below 800°C, TiO2 and Al2O3 start to consume at 900 and 1100°C, respectively. BaTi4O9 phase appears at 1000°C while BaAl2Ti5O14 phase starts to reveal at 1200°C. As the temperature increases, the density, dielectric constant and quality factor of the BaAl2Ti5O14 ceramic increase and keep unchanged at 1350°C. The dielectric properties of BaAl2Ti5O14 ceramic sintered at 1350°C for 3h are: εr=35.8, Q×f=5130GHz, τf=-6.8ppm/°C.

Cite this paper
X. Yao, W. Chen and L. Luo, "The Reaction Sequence and Dielectric Properties of BaAl2Ti5O14 Ceramics," Advances in Materials Physics and Chemistry, Vol. 2 No. 4, 2012, pp. 28-30. doi: 10.4236/ampc.2012.24B008.
References
[1]   R. Cava, “Dielectric materials for applications in microwave communications,” J.Mater.Chem. pp. 54-62, 2001.

[2]   I. Reaney,D. Iddles, “Microwave dielectric ceramics for resonators and filters in mobile phone networks,” J.Am.Ceram.Soc.pp.2063-2072,2006.

[3]   [3] H. Ohsato, “Science of tungstenbronze-type like Ba6-3xR8+2xTi18 O54 (R=rare earth) microwave dielectric solid solutions,” J.Euro. Ceram. Soc. pp.2703-2711,2001.

[4]   H. Ohsato, M. Mizuta, “Microwave dielectric properties of tungsten bronze-type Ba6-3xR8+2xTi18O54 (R=La, Pr, Nd and Sm) solid solution,”J. Ceram.Soc.Jap.pp.178-182,1998.

[5]   J. Zhu, E. Kipkoech, W. Lu. “Effects of LnAlO3(Ln=La, Nd, Sm) additives on the properties of Ba4.2Nd9.2Ti18O54 ceramics,” J.Euro.Ceram.Soc.pp.2027-2030,2006.

[6]   H. Ohsato, A. Komura, “Microwave dielectric properties and sintering of Ba6-3xR8+2xTi18O54 (R=Sm,x=2/3) solid solution with added rutile,” Jpn.J.Appl.Phys. pp.5357-5359,1998.

[7]   X. Yao, H. Lin, “Antireducion of Ti4+ in Ba4.2Sm9.2Ti18O54 ceramics by doping with MgO,Al2O3 and MnO2,”Ceram.Int.pp.3011-3016,2012

 
 
Top