The Effect of Ageing Time on Some Mechanical Properties of Aluminum/0.5% Glass Reinforced Particulate Composite
ABSTRACT
A particulate-hardened composite usually known as cermets with aluminum matrix and reinforced with ceramic particles from broken bottles was used to investigate the effect of ageing time on hardness and tensile strength. The samples used for the work were produced using stir-cast method and the samples were cast in metal moulds to improve on the surface finish and to obtain good cooling rate. The composite composition used was Al/0.5% glass particles. The samples were treated at 500?C and quenched in water at 65?C. They were then aged at various temperatures ranging from 150?C - 210?C. The result of the hardness test showed that within the range of the ageing time selected the hardness increased with the ageing for all the ageing temperatures used. Variations were observed but this is normal in ageing, particularly when coherent and incoherent precipitates are formed at a point in time, or when over-ageing occurs. The plot of the tensile strength tests and the hardness tests, with ageing time showed the trend as observed. The highest hardness value of 37.3 HRB occurred after 5 hours of ageing likewise the highest tensile strength value of 398.36 N/mm2 occurred after 5 hours of ageing at the same ageing temperature of 190?C. The aged composite showed improved hardness and tensile strength when compared to as-cast value of 23.7 HRB for hardness and 253.12 N/mm2 for tensile strength respectively.

Cite this paper
A. Ihom, N. Bem, E. Anbua and J. Ogbodo, "The Effect of Ageing Time on Some Mechanical Properties of Aluminum/0.5% Glass Reinforced Particulate Composite," Journal of Minerals and Materials Characterization and Engineering, Vol. 11 No. 9, 2012, pp. 919-923. doi: 10.4236/jmmce.2012.119089.
References
[1]   M. K. Suprappa, “Aluminum Matrix Composites: Challenges and Opportunities,” Sadhana, Vol. 28, No. 1-2, 2003, pp. 319-334. doi:10.1007/BF02717141

[2]   Http:/umewww.epf/ch/people/cayron/Fichiers/thesebook-hap.2pdf.

[3]   G. Curran, “MMCs, The Future,” Materials World, Vol. 6, No. 1, 1998, pp. 21-22.

[4]   M. Gupta, “Recycling of Aluminum Based Composite using Disintegrated Melt Deposition Technique,” National University of Singapore, Engineering Research, Vol. 23, No. 1, 2008.

[5]   ASM Committee on Gas Carburizing, “Carburizing and Carbonitriding,” American Society for Metals, 1977, pp. 6-20.

[6]   J. W. Martin, “Precipitation Hardening,” Second Edition, Butterworth Heinemann, 1998.

[7]   R. A. Higgins, “Properties of Engineering Materials,” 5th Edition, Hodder and Stoughton, London, 1983.

[8]   S. B. Hassan, O. Aponbiede and V. S. Aigbodion, “Precipitation Hardening Characteristics of Al-Si-Fe/SiC Particulate Composite,” Journal of Alloys and Compounds, Vol. 466, No. 1-2, 2008, pp. 268-272. doi:10.1016/j.jallcom.2007.11.023

[9]   S. B. Hassan and V. S. Aigbodion, “The Effect of Thermal Ageing on Microstructure and Mechanical Properties of Al-Si-Fe/Mg Alloys,” Journal of Alloys and Compounds, Vol. 486, No. 1-2, 2009, pp. 309-314. doi:10.1016/j.jallcom.2009.06.131

[10]   G. E. Dieter, “Mechanical Metallurgy,” 3rd Edition, MCgraw-Hill Book Company, London, 1988.

[11]   M. H. Mohammad, T. M. Ahmad, M. H. Adel and T. H. Mohammad, “The Effect of Time, Percent of Copper and Nickel on Naturally Aged Al-Cu-Ni Cast Alloys,” JMMCE, Vol. 11, No. 2, 2012, pp. 117-131.

[12]   O. A. Alo, L. E. Umoru, J. A. Ajao and K. M. Oluwasegun, “Thermal, Hardness, and Microstructural Characterization of Al-Si-SiCp Composites,” JMMCE, Vol. 11, No. 2, 2012, pp. 159-168.

 
 
Top