The Effects of an Applied Voltage on the Corrosion Characteristics of Dense MgO
Abstract
In a recent investigation Mills and Riaz [1] showed that industrial oxide refractory corrosion by liquid oxides could be changed by the application of a small voltage across the liquid oxide-refractory interface. They explained their result in terms of penetration of the refractory pores with liquid oxide. Their analysis of the corrosion effect was to some degree limited by the use of an industrial refractory material in the study. Further, it was not clear whether their findings were limited to solely industrial refractories or had wider ranging application to more dense ceramic type solid oxide systems. In this study, a simpler and more easily characterized solid oxide (dense MgO) has been used to examine the effects of an applied voltage on the solid oxide in a liquid oxide melt. The dissolution rate of an MgO ceramic in a CaO-SiO2-Al2O3 and CaO-SiO2- Fe2O3-FeO-MgO liquid oxide composition at various applied voltages has been measured at 1540°C. It was found that the MgO corrosion in the CaO-SiO2-Al2O3 system was insensitive to an applied voltage over the voltage range –0.5 to 0.3 V. In the CaO-SiO2-Fe2O3-FeO-MgO liquid oxide system the MgO corrosion rate showed a maximum at –0.45 V. This effect has been explained by considering the consequences of an applied voltage on the rate of Marangoni flow at the liquid oxide-refractory-gas interface and in turn, the flow effect on the rate of the mass transfer controlled MgO dissolution reaction.

Cite this paper
B. Monaghan, S. Nightingale, Q. Dong and M. Funcik, "The Effects of an Applied Voltage on the Corrosion Characteristics of Dense MgO," Engineering, Vol. 2 No. 7, 2010, pp. 496-501. doi: 10.4236/eng.2010.27065.
References

[1]   S. Riaz, K. C. Mills and K. Bain, “Experimental Exami-nation of Liquid Oxide/Refractory Interface,” Ironmaking and Steelmaking, Vol. 29, No. 2, 2002, pp. 107-113.

[2]   W. E. Lee and S. Zhang, “Melt Corrosion of Oxide and Oxide-Carbon Refractories,” International Materials Re-views, Vol. 44, No. 3, 1999, pp. 77-104.

[3]   A. A. Kazakov, “Influence of the Electrical Potential on Converter Smelting,” Russian Metallurgy, Vol. 6, 1997, pp. 25-29.

[4]   R. R. Dogonadze and Y. A. Chizmadzhev, “Structure and Capacitance of the Metal-Fused Salt,” Interface Pro-ceedings Academy of Sciences USSR Physical Chemical Section, Vol. 157, No. 944, 1964, pp.778-781.

[5]   E. A. Ukshe, N. G. Bukun, D. I. Leikis and A. N. Frum-kin, “Investigation of the Electric Double Layer in Salt Melts,” Electrochimica Acta, Vol. 9, No. 4, 1964, pp. 431-439.

[6]   M. Vallet and B. Berge, “Electrowetting of Water and Aqueous Solutions on Poly(Ethylene Terephthalate) In-sulating Films,” Polymer, Vol. 37, No. 12, 1996, pp. 2465-2470.

[7]   F. D. Richardson, “Physical Chemistry of Melts in Metal-lurgy,” Academic Press, London, UK, 1974.

[8]   A. D. Graves, G. J. Hill and D. Inman, “Electrode Processes in Molten Salts,” Advances in Electrochemistry and Electrochemical Engineering, Vol. 4, No. 117, 1966, pp. 159-159.

[9]   K. C. Mills, “Liquid Oxide Atlas,” 2nd Edition, Verlag Stalheisen GmBH, Dusseldorf, Germany, 1995.

[10]   N. Eustathopoulos, M. G. Nicholas and B. Drevet, “Wet-tability at High Temperatures,” 12th Edition, Pergamon Press, London, UK, 1999.

[11]   B. J. Monaghan, S. A. Nightingale, L. Chen and G. A. Brooks, “The Dissolution Behavior of Selected Oxides in CaO-SiO2-Al2O3 Liquid Oxides,” VII International Con-ferance on Molten Liquid oxides and Fluxes and Salts, SAIMM, Johannesburg, South Africa, 2004, pp. 585-594.

[12]   S. A. Nightingale, G. A. Brooks and B. J. Monaghan, “Degradation of MgO Refractory in CaO-SiO2-MgO- FeOx and CaO-SiO2-Al2O3-MgO-FeOx Liquid Oxides under Forced Convection,” Metallurgical and Materials Transactions B, Vol. 36B, No. 4, 2005, pp. 453-461.

[13]   M. Ashizuka and K. Oe, “Measurement of the Electrical Capacitance of the Double Layer at the Interface between CaO-SiO2, CaO-SiO2-Al2O3 and CaO-Al2O3 Oxide Melts,” Journal of the Japanese Institute of Metals, Vol. 39, No. 12, 1975, pp. 1243-1249.

[14]   K. Mukai, “Wetting and Marangoni Effect in Iron and Steelmaking Processes,” ISIJ International, Vol. 32, No. 1, 1992, pp. 19-25.

[15]   M. Ashizuka and K. Oe, “On the Capacitance of Platinum Electrode in Na2O-SiO2 Melts,” Journal of the Japanese Institute of Metals, Vol. 39, No. 4, 1975, pp. 388-393.

[16]   T. Emi, T. Sakuraya and K Sanbongi, “Electrochemical Studies of the Interfacial Phenomena at Metal/Molten Liquid Oxide Boundaries,” The 4th Japan–USSR Joint Symposium on the Physical Chemistry of Metallurgical Processes, The Iron and Steel Institute, Tokyo, Japan, 1973, pp. 72-86.

 
 
Top