Corrosion Behavior of Nanostructured TiAlN and AlCrN Hard Coatings on Superfer 800H Superalloy in Simulated Marine Environment
Affiliation(s)
Metallurgical & Materials Engineering Department, I.I.T. Roorkee, Roorkee-247667, India. Mechanical Engineering Department, Y.C.E., Talwandi Saboo-151302,India.
Metallurgical & Materials Engineering Department, I.I.T. Roorkee, Roorkee-247667, India. Mechanical Engineering Department, Y.C.E., Talwandi Saboo-151302,India.
ABSTRACT
In this work, TiAlN and AlCrN coatings were deposited on Superfer 800H superalloy using Balzer’s rapid coating system (RCS) machine (make Oerlikon Balzers, Swiss) under a reactive nitrogen atmosphere. The corrosion resistance of the substrate, TiAlN and AlCrN coated samples in a 5 wt% NaCl solution was evaluated and compared by salt fog (spray) test for 24 hrs, 48 hrs and 72 hrs. The samples were monitored and analyzed by using weight loss measurement, XRD and SEM/EDAX techniques. There was no weight loss observed for coated as well as uncoated specimens in all test conditions.
In this work, TiAlN and AlCrN coatings were deposited on Superfer 800H superalloy using Balzer’s rapid coating system (RCS) machine (make Oerlikon Balzers, Swiss) under a reactive nitrogen atmosphere. The corrosion resistance of the substrate, TiAlN and AlCrN coated samples in a 5 wt% NaCl solution was evaluated and compared by salt fog (spray) test for 24 hrs, 48 hrs and 72 hrs. The samples were monitored and analyzed by using weight loss measurement, XRD and SEM/EDAX techniques. There was no weight loss observed for coated as well as uncoated specimens in all test conditions.
Cite this paper
V. Chawla, D. Puri, S. Prakash and B. Sidhu, "Corrosion Behavior of Nanostructured TiAlN and AlCrN Hard Coatings on Superfer 800H Superalloy in Simulated Marine Environment," Journal of Minerals and Materials Characterization and Engineering, Vol. 8 No. 9, 2009, pp. 693-700. doi: 10.4236/jmmce.2009.89060.
V. Chawla, D. Puri, S. Prakash and B. Sidhu, "Corrosion Behavior of Nanostructured TiAlN and AlCrN Hard Coatings on Superfer 800H Superalloy in Simulated Marine Environment," Journal of Minerals and Materials Characterization and Engineering, Vol. 8 No. 9, 2009, pp. 693-700. doi: 10.4236/jmmce.2009.89060.
References
[1] Li Liu, Ying Li and Fuhui Wang; Electrochimica Acta; 2007; 52; 2392-2400. [2] Gadadhar Sahoo and R. Balasubramaniam; Journal of ASTM International;2008; Vol.5, No. 5, Paper ID JaI101191. [3] R.A. Mahesh, R. Jayaganthan, S. Prakash; J Alloys and Compounds; 2009; 468 ; 392-405. [4] Corvo, F., Betancourt, N., and Mendoza, A.; Corrosion Science; 1995; 37; 1889-1901. [5] L. A. Dobrzanski, Z. Brytan, M. Actis Grande, M. Rosso; Journal of Materials Processing Technology; 2007; 192-193; 443-448. [6] Vikas Chawla, Buta Singh Sidhu, D. Puri and S. Prakash, J of the Australian ceramic society; 2008; 42; 56-62. [7] Vikas Chawla, S. Prakash and B.S. Sidhu; Materials and Manufacturing Processes; 2007; 22 ; 469-473.
[1] Li Liu, Ying Li and Fuhui Wang; Electrochimica Acta; 2007; 52; 2392-2400. [2] Gadadhar Sahoo and R. Balasubramaniam; Journal of ASTM International;2008; Vol.5, No. 5, Paper ID JaI101191. [3] R.A. Mahesh, R. Jayaganthan, S. Prakash; J Alloys and Compounds; 2009; 468 ; 392-405. [4] Corvo, F., Betancourt, N., and Mendoza, A.; Corrosion Science; 1995; 37; 1889-1901. [5] L. A. Dobrzanski, Z. Brytan, M. Actis Grande, M. Rosso; Journal of Materials Processing Technology; 2007; 192-193; 443-448. [6] Vikas Chawla, Buta Singh Sidhu, D. Puri and S. Prakash, J of the Australian ceramic society; 2008; 42; 56-62. [7] Vikas Chawla, S. Prakash and B.S. Sidhu; Materials and Manufacturing Processes; 2007; 22 ; 469-473.