New Methods Testing of Adhesion of the Coating to Sheet Metal by Bending
ABSTRACT
The article is deals for new experimental equipment for effective test adhesion for selected coating STEEL, applied cold on the coated metal sheet with Al (aluminum). Explanation to the word STEEL: STEEL coating has significant anti- corrosive properties and he is resistant for main oxidizing agents such as acids, alkalis, salt vapors etc. Resists tem- peratures to 600?C and create an elastic film that is resistant to abrasion, as soon as it was to complete po-lymerization. It is very simple to applied to metallic and nonmetallic surfaces. Dries quickly and is dry to the touch after 90 to 120 seconds. STEEL is the best possible solution anywhere, if needs arises powerful local protection against atmospheric and corrosive agents or to elevated temperatures. STEEL is also useful as a method for protect of welds on stainless steels instead of traditional staining procedures. Broad application is in automotive industry to modify the surfaces of block vehicle, car-body repairs, welds needing protection, in heating industry for example boilers, in air condition with heat exchanger and in shipping industry. [1-3].In experiments with a new test equipment is showed that for bending radius of interval from range R11 to R35 there is a change deposited coating STEEL from original coating Al and this coating was part of test metal sheet of thickness 1.5 mm. In the next stage of solution was developed technological process, which allowed increase of adhesion coating STEEL for bending up to or maximum 180? (shape U). Result of new technology is documented in article. Experiments was implementing with cooperation of the Masaryk University in Brno.

Cite this paper
M. Dvořák and E. Schwarzer, "New Methods Testing of Adhesion of the Coating to Sheet Metal by Bending," Journal of Surface Engineered Materials and Advanced Technology, Vol. 2 No. 2, 2012, pp. 61-64. doi: 10.4236/jsemat.2012.22011.
References
[1]   A. Sarani, A. Y. Nikiforov and C. Leys, “Low-Temperature Plasmas, Plasma Applications, Plasma Sources, Sheaths,” Physics of Plasmas, Vol. 17, No. 6, 2010, pp. 063504-063511. doi:10.1063/1.3439685

[2]   D. H. Shin, C. U. Bang, J. H. Kim, Y. C. Hong, H. S. Uhm, D. K. Park and K. H. Kim, “Treatment of Metal Surface by Atmospheric Microwave Plasma Jet,” IEEE Transactions on Plasma Science, Vol. 34, No. 4, 2006, pp. 1241-1246. doi:10.1109/TPS.2006.876486

[3]   B. M. Akram, K. M. B. Jansen, L. J. Ernst and S. Bhow- mik, “Atmospheric Pressure Plasma Surface Modification of Titanium for High Temperature Adhesive Bonding,” International Journal of Adhesion and Adhesives, Vol. 31, No. 7, 2011, pp. 598-604. doi:10.1016/j.ijadhadh.2011.05.009

[4]   M. Mare?ková and M. Dvo?ák, “Effect of Bending on the Quality of Zinc Coating on Steel Sheet,” Bratislava, 2009, pp. 67-70.

[5]   ?SN EN ISO 7438, “Metallic Materials—Bend Test,” Czech Standards Institute, 2005.

[6]   ?SN ISO 24213, “Metallic Materials—Sheets and Belt: Evaluation Method of Suspension for Flexural Bending,” Czech Standards Institute, 2009.

[7]   ?SN EN 13144, “Metallic and Other Inorganic Coatings: Method for Quantitative Measurement of Adhesion for Tensile Test,” Czech Standards Institute, 2003.

[8]   T. Blanks, “Metals Handbook: Mechanical Testing,” American Society for Metals, 1985.

[9]   M. Dvo?ák, et al., “Technology II,” Academic Publishing CERM, Ltd., Brno, 2001.

[10]   V. Kreibich, “Theory and Technology of Surface Treatment,” Publishing House of CTU, Prague, 1996.

[11]   V. Krej?ík, “Surface Treatment of Metals II,” Publishing House of Technical Literature, Prague, 1988.

[12]   ?SN EN ISO 20482, “Metallic Materials—Sheet and Belts—Bulge Tests According to Erichsen,” Czech Standards Institute, Prague, 2004.

[13]   ?SN EN ISO 1519, “Paints Substance—Bend Test (Cylindrical Mandrel),” Czech Standards Institute, 2002.

[14]   M. Dvo?ák, M. Hu?ek and E. Schwarzer, “New Methods Testing of Adhesion of the Coating to Sheet Metal by Bending,” Union Forges CZ j.s.c., Brno, 2010, pp. 81-84.

[15]   M. Dvo?ák, M. Hu?ek and E. Schwarzer, “Testing of Adhesion of the Coating to Sheet Metal by Bending,” MM Publishing Ltd., Prague, 2010, pp. 22-23.

[16]   M. Hu?ek and M. Dvo?ák, “Adhesion Test of Multi-Functional Coating Al-Zn,” STU, Bratislava, 2009, pp. 63-71.

[17]   M. Hu?ek and M. Dvo?ák, “Adhesion Test of Multi-Functional Coating on the Plate Using Graduated Bending jig,” Engineering Technology, No. 2, 2010, pp. 15-19.

[18]   M. Klíma, Z. Muziká?, M. Dvo?ák and M. Alberti, “Surface Treatment by Low-Temperature Non-Isothermal Plasma at Atmospheric Pressure,” 41th International Conference on Paints, University Pardubice, 2010, pp. 251- 262.

[19]   Masaryk University, “Method of Making a Physically and Chemically Active Environment by Means of a Plasma Jet and the Related Plasma Jet,” Patent EP 1077021, 2005.

 
 
Top