Synthesis Sol-Gel Derived Highly Transparent ZnO Thin Films for Optoelectronic Applications
ABSTRACT
In this work, ZnO thin films were derived by sol-gel using two different techniques; dip coating and spin coating technique. The films were deposited onto glass substrate at room temperature using sol-gel composed from zinc acetate dehydrate, monoethanolamine, isopropanole, and de-ionized water, the films were preheated at 225?C for 15 min. The crystallographic structures of ZnO films were investigated using X-ray diffraction (XRD); the result shows that the good film was prepared at dip coating technique, it was polycrystalline and highly c-orientation along (002) plane, the lattice constant ratio (c/a) was calculated at (002), it was about 1.56. The structure of thin films, prepared by spin coating technique, was amorphous with low intensity and wide peaks. The optical properties of the prepared film were studied using UV-VIS spectrophotometer with the range 190 - 850 nm, and by using the fluorescence spectrometer. The optical characterization of ZnO thin films that were prepared by the dip coating method have good transmittance of about 92% in the visible region, it can be noted from the fluorescence spectrometer two broad visible emission bands centered at 380nm and 430 nm. The optical energy gaps for the direct and indirect allowed transitions were calculated, the values were equal 3.2 eV and 3.1 eV respectively. Dip coating technique create ZnO films with potential for application as transparent electrodes in optoelectronic devices such as solar cell.

Cite this paper
W. R. Saleh, N. M. Saeed, W. A. Twej and M. Alwan, "Synthesis Sol-Gel Derived Highly Transparent ZnO Thin Films for Optoelectronic Applications," Advances in Materials Physics and Chemistry, Vol. 2 No. 1, 2012, pp. 11-16. doi: 10.4236/ampc.2012.21002.
References
[1]   G. G. Valle, P. Hammer, S. H. Pulcinelli and C. V. Santilli, “Transparent and Conductive ZnO:Al Thin Films Prepared by Sol-Gel Dip-Coating,” Journal of European Ceramic Society, Vol. 24, No. 6, 2004, pp. 1009-1013. doi:10.1016/S0955-2219(03)00597-1

[2]   T. A. Krajewski, K. Dybko and G. ?uka, “Dimethylzinc and Diethylxinc as Precur-sors for Monocrystalline Zinc Oxide Grow by Atomic Layer Deposition,” The European Materials Research Society Fall Meeting, Symposium C, Warsaw, 14-18 September 2009.

[3]   M. S. Wang, K. E. Lee and S. H. Hahn, “Optical and Photoluminescent Properties of Sol-Gel Al-Doped ZnO Thin Films,” Materials Letters, Vol. 61, No. 4-5, 2007, pp. 1118-1121. doi:10.1016/j.matlet.2006.06.065

[4]   M. Al-hamed and W. Abdullah, “Structural and Optical Properties of ZnO:Al Films Prepared by the Sol-Gel Method,” Journal of Electron Devices, Vol. 7, 2010, pp. 246- 252.

[5]   F. E. Ghodsi and H. Absalan, “Comparative Study of ZnO Thin Films Prepared by Different Sol-Gel Route,” Thin Solid Films, Vol. 118, No. 4, 2010, pp. 629-664.

[6]   X.-B. Lou, H.-L. Shen and H. Zhang, “Optical Properties of Nanosized ZnO Films Prepared by Sol-Gel Process,” Transactions of Nonferrous Metals Soci-ety of China, Vol. 17, 2007, pp. 814-817.

[7]   N. Shakti and P. S. Gupta, “Structural and Optical Prop- erties of Sol-Gel Pre-pared ZnO Thin Film,” Applied Phy- sics Research, Vol. 2, No. 1, 2010, pp. 19-28.

[8]   C. J. Brinker and G. W. Sherer, “Sol-Gel Science,” Academic Press, San Diego, 1990.

[9]   E. Miorin, C. Pagura, M. Battagliarin, M. Guglielmi and P. Miselli, “Stain-Resistant Sol-Gel Silica Coatings on Stoneware Tile,” America Ceramic Society Bulletin, Vol. 82, No. 3, 2003, pp. 52-57.

[10]   H. Schmidt and M. Mennig, “The Sol-Gel Gate-way,” Instit für Neue Materialien (INM), Saarbrücken, 2000. http://www.solgel.com/articles/Nov00/mennig.htm

[11]   M. Ren, Z. Mal and Y. Lu, “The Effect of the Thermal Annealing on ZnO Thin Films Grown by Pulsed Laser Deposition,” Journal of Applied Physics, Vol. 88, No. 1, 2000, pp. 498-502. doi:10.1063/1.373685

[12]   K. Kim, et al., “Realization of p-Type ZnO Thin Films,” Applied Physics Letters, Vol. 83, No. 1, 2003, pp. 63-65. doi:10.1063/1.1591064

[13]   C. J. Brinker and G. W. Scherer, “The Physics and Chemistry of Sol-Gel Processing,” Academic Press Inc., San Diego, 1990.

[14]   C. Gumu, O. M. Ozkendir, H. Kavak and Y. Ufuktepe, “Structural and Optical Properties of Zinc Oxide Thin Films Prepared by Spray Pyrolysis Method,” Journal of Optoelectronics and Advanced Materials, Vol. 8, No. 1, 2006, pp. 299-303.

[15]   F. I. Ezama, “Fabrication, Optical Properties and Applications of Undoped Chemical Bath Deposited ZnO Thin Films,” Journal of Research (Science), Vol. 15, No. 4, 2004, pp. 343-350.

[16]   C. X. Xu, G. P. Zhu, X. Li, Y. Yang, S. T. Tan, X. W. Sun, C. Lincoln and T. A. Smith, “Growth and Spectral Analysis of ZnO Nanotubes,” Journal of Applied Physics, Vol. 103, No. 9, 2008, Article ID: 094303. doi:10.1063/1.2908189

[17]   K. Yoshino, T. Fukushima and M. Yoneta, “Structural, Optical and Electrical Characterization on ZnO Film Grown by a Spray Pyrolysis Method,” Journal of Materials Science: Materials in Electronics, Vol. 16, No. 7, 2005, pp. 403-408. doi:10.1007/s10854-005-2305-5

 
 
Top